HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITE®

Preliminary

E GF 15 ECO black (8327)

E GF 15 ECO

PRECITE® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

6.300MPa

Strength

110MPa

Impact

35kJ/m²

PRECITE® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

NEXT S3 GF 30 S1 black (8887)

PA610-I GF30

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

Modulus

7.800MPa

Strength

135MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

AKROMID®

A3 S1 black (1071)

PA66-I

AKROMID® A3 S1 black 950089 (1071) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/m²

AKROMID® A3 S1 black 950089 (1071) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

AKROLEN®

PP GFM 25/15 black (1415)

PP (GF25+M15)

AKROLEN® PP GFM 25/15 black (1415) is a 25% glass fibre reinforced, 15% mineral-filled polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 black (1415) is a 25% glass fibre reinforced, 15% mineral-filled polypropylene with good surface and dimensional stability.

AKROMID®

A3 GK 40 1 natural (1803)

PA66 GB40

AKROMID® A3 GK 40 1 natural (1803) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

Modulus

5.500MPa

Strength

95MPa

Impact

25kJ/m²

AKROMID® A3 GK 40 1 natural (1803) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

AKROMID®

A3 GF 35 1 black (2269)

PA66 GF35

AKROMID® A3 GF 35 1 black (2269) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.600MPa

Strength

215MPa

Impact

92kJ/m²

AKROMID® A3 GF 35 1 black (2269) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 30 S1 black (2091)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (2091) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID® B3 GF 30 S1 black (2091) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

130313280

AKROMID®

Preliminary

A3 black (7557)PA66

AKROMID® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

Properties

Modulus

3.200MPa

Strength

80MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3200 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
80 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 10 %
> 25 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
4 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
65 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
210 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
45 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,14 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,9 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
310 mm
980 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.