PRECITE®

Preliminary

K GF 15 ECO black (8328)

PBT-PET- GF 15

PRECITE® K GF 15 ECO black (8328) - PBT/PET blend, recycled PET content, 30% glass fiber, good strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

5.900MPa

Strength

105MPa

Impact

35kJ/m²

PRECITE® K GF 15 ECO black (8328) - PBT/PET blend, recycled PET content, 30% glass fiber, good strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROMID®

NEXT S3 GF 30 S1 black (8887)

PA610-I GF30

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

Modulus

7.800MPa

Strength

135MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

AKROLEN®

PP GFM 25/15 black (1415)

PP (GF25+M15)

AKROLEN® PP GFM 25/15 black (1415) is a 25% glass fibre reinforced, 15% mineral-filled polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 black (1415) is a 25% glass fibre reinforced, 15% mineral-filled polypropylene with good surface and dimensional stability.

AKROMID®

A3 S1 black (1071)

PA66-I

AKROMID® A3 S1 black 950089 (1071) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/m²

AKROMID® A3 S1 black 950089 (1071) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

AKROMID®

A3 GK 40 1 natural (1803)

PA66 GB40

AKROMID® A3 GK 40 1 natural (1803) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

Modulus

5.500MPa

Strength

95MPa

Impact

25kJ/m²

AKROMID® A3 GK 40 1 natural (1803) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

AKROMID®

B3 GF 30 S1 black (2091)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (2091) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID® B3 GF 30 S1 black (2091) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMID®

A3 GF 35 1 black (2269)

PA66 GF35

AKROMID® A3 GF 35 1 black (2269) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.600MPa

Strength

215MPa

Impact

92kJ/m²

AKROMID® A3 GF 35 1 black (2269) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

130313280

AKROMID®

B3 GF 45 1 black (3851)PA6 GF45

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Features

heat stabilised 130

Properties

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14500 MPa
8500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,5 %
8,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
13000 MPa
7500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
315 MPa
200 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
4,5 %
6,7 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
110 kJ/m²
108 kJ/m²
95 kJ/m²
108 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
20 kJ/m²
25 kJ/m²
16 kJ/m²
15 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
145 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,5 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.