Description

AKROMID®

NEXT S3 GF 30 S1 black (8887)

PA610-I GF30

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

Modulus

7.800MPa

Strength

135MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

PRECITE®

Preliminary

E GF 15 ECO black (8327)

E GF 15 ECO

PRECITE® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

6.300MPa

Strength

110MPa

Impact

35kJ/m²

PRECITE® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROLEN®

PP GFM 25/15 black (1415)

PP (GF25+M15)

AKROLEN® PP GFM 25/15 black (1415) is a 25% glass fibre reinforced, 15% mineral-filled polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 black (1415) is a 25% glass fibre reinforced, 15% mineral-filled polypropylene with good surface and dimensional stability.

AKROMID®

A3 S1 black (1071)

PA66-I

AKROMID® A3 S1 black 950089 (1071) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/m²

AKROMID® A3 S1 black 950089 (1071) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

AKROMID®

A3 GF 35 1 black (2269)

PA66 GF35

AKROMID® A3 GF 35 1 black (2269) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.600MPa

Strength

215MPa

Impact

92kJ/m²

AKROMID® A3 GF 35 1 black (2269) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GK 40 1 natural (1803)

PA66 GB40

AKROMID® A3 GK 40 1 natural (1803) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

Modulus

5.500MPa

Strength

95MPa

Impact

25kJ/m²

AKROMID® A3 GK 40 1 natural (1803) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

AKROMID®

B3 GK 50 black (2311)

PA6 GB50

AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage

Modulus

5.700MPa

Strength

75MPa

Impact

42kJ/m²

AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage

130313280

AKROMID®

A3 GF 25 1 natural (2390)PA66 GF25

AKROMID® A3 GF 25 1 natural (2390) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength and light inherent color.

Features

heat stabilised 130

Properties

Modulus

8.500MPa

Strength

185MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8500 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
115 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,6 %
6,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
7600 MPa
6200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
260 MPa
200 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
70 kJ/m²
90 kJ/m²
64 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
10 kJ/m²
13 kJ/m²
9 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
225 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 °C
130 - 150 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,32 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,0 - 2,2 %

Water absorption

ISO 62

23°C, saturated
5,7 - 6,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 %
1,3 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more