AKROMID®

UL

B3 GF 40 1 HU black (8415)

PA6 GF40

AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.

PRECITE®

Preliminary

E GF 15 ECO black (8327)

E GF 15 ECO

PRECITE® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

6.300MPa

Strength

110MPa

Impact

35kJ/m²

PRECITE® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITE®

Preliminary

P3 GF 15 4 natural (8429)

PBT-I GF15

PRECITE®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

Modulus

5.000MPa

Strength

85MPa

Impact

55kJ/m²

PRECITE®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

AKROTEK®

Preliminary

PK-VM GF 50 natural (8683)

PK GF50

AKROTEK® PK-VM GF 50 natural (8683) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

14.500MPa

Strength

190MPa

Impact

80kJ/m²

AKROTEK® PK-VM GF 50 natural (8683) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

C28 GF 25 FRT grey (8133)

PA-Blend

AKROMID® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

150MPa

Impact

NA

AKROMID® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.

PRECITE®

Preliminary

K GF 50 8 black (8446)

PBT+PET GF50

PRECITE® K GF 50 8 black (8446) - PBT/PET blend, 50% glass fibre, very high strength, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

Modulus

17.500MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® K GF 50 8 black (8446) - PBT/PET blend, 50% glass fibre, very high strength, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

AKROMID®

Preliminary

B28 GM 10/20 6 black (8640)

PA6 (GF10+GB20)

B28 GM 10/20 6 black (8640) - PA 6 with 10% glass fibers and 20% glass beads reinforced, easy flowing with good surface properties.

Modulus

5.500MPa

Strength

100MPa

Impact

50kJ/m²

B28 GM 10/20 6 black (8640) - PA 6 with 10% glass fibers and 20% glass beads reinforced, easy flowing with good surface properties.

129303180

AKROLOY®

PA LGF 50 natural (5504)PA66+PA6I/6T LGF50

AKROLOY® PA LGF 50 natural (5504) is a 50% long glass fibre reinforced, semi-aromatic polyamide blend with extraordinary high stiffness and strength even at high temperature and very high impact and notched impact strength at elevated and low temperature even in conditioned state. PA LGF 50 natural (5504) distinguish due to isotropic mechanical properties, low shrinkage, higher heat deflection temperature and very good fatigue performance. The material has very good surface properties.

Features

low warpage
reduced moisture

Properties

Modulus

19.000MPa

Strength

290MPa

Impact

100kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
19000 MPa
18500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
290 MPa
265 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
2,3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
17500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
440 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
105 kJ/m²
85 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
42 kJ/m²
42 kJ/m²
45 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,59 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,2 - 1,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more