PRECITE®

Preliminary

P3 GF 20 8 natural (8456)

PBT GF20

PRECITE® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

Modulus

7.200MPa

Strength

125MPa

Impact

65kJ/m²

PRECITE® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

PRECITE®

Preliminary

K GF 50 8 black (8446)

PBT+PET GF50

PRECITE® K GF 50 8 black (8446) - PBT/PET blend, 50% glass fibre, very high strength, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

Modulus

17.500MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® K GF 50 8 black (8446) - PBT/PET blend, 50% glass fibre, very high strength, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

AKROMID®

UL

B3 GF 40 1 HU black (8415)

PA6 GF40

AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.

PRECITE®

Preliminary

K GF 15 ECO black (8328)

PBT-PET- GF 15

PRECITE® K GF 15 ECO black (8328) - PBT/PET blend, recycled PET content, 30% glass fiber, good strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

5.900MPa

Strength

105MPa

Impact

35kJ/m²

PRECITE® K GF 15 ECO black (8328) - PBT/PET blend, recycled PET content, 30% glass fiber, good strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROMID®

NEXT S3 GF 30 S1 black (8887)

PA610-I GF30

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

Modulus

7.800MPa

Strength

135MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

PRECITE®

Preliminary

E GF 15 ECO black (8327)

E GF 15 ECO

PRECITE® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

6.300MPa

Strength

110MPa

Impact

35kJ/m²

PRECITE® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITE®

Preliminary

P3 GF 15 4 natural (8429)

PBT-I GF15

PRECITE®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

Modulus

5.000MPa

Strength

85MPa

Impact

55kJ/m²

PRECITE®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

129303180

AKROMID®

S3 1 black (3317)PA610

AKROMID® S3 1 black (3317) is a nonreinforced and heat stabilised polyamide 6.10 with lower moisture absorption and high chemical resistance.

Features

heat stabilised 130
reduced moisture

Properties

Modulus

2.400MPa

Strength

70MPa

Impact

180kJ/m²

Sustainability

Biobased carbon content

60 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2400 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
70 MPa
50 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
4,5 %
20 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 50 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
1900 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
100 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
4 kJ/m²
12 kJ/m²
4 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
125 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
55 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,08 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
1,6 %
1,8 %

Rheological Properties

MVR

ISO 1133

275°C/2,16kg
10 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.