HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

A3 1 S3 black (21002)

PA66-I

AKROMID® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

PRECITE®

Preliminary

P3 GK 30 natural (7643)

PBT GK30

PRECITE® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

Modulus

3.900MPa

Strength

50MPa

Impact

25kJ/m²

PRECITE® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

PRECITE®

Preliminary

E GF 50 black (7395)

PET GF50

PRECITE® E GF 50 black (7395) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

18.000MPa

Strength

210MPa

Impact

60kJ/m²

PRECITE® E GF 50 black (7395) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

A3 GF 35 2 black (21010)

PA66 GF35

AKROMID® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

Modulus

12.000MPa

Strength

185MPa

Impact

50kJ/m²

AKROMID® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

PRECITE®

Preliminary

E GF 30 black (7814)

PET GF30

PRECITE® E GF 30 black (7814) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

11.000MPa

Strength

170MPa

Impact

50kJ/m²

PRECITE® E GF 30 black (7814) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

UL
Preliminary

B28 GF 30 9 FR natural (8069)

PA6 GF 30 FR(40)

AKROMID® B28 GF 30 9 FR natural (8069) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

144MPa

Impact

80kJ/m²

AKROMID® B28 GF 30 9 FR natural (8069) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

Preliminary

B3 GF 50 6 black (20028)

PA6 GF50

AKROMID® B3 GF 50 6 black (20028) is a 50% glass fibre reinforced, inorganic high temperature stabilised polyamide 6 with very high stiffness and strength

Modulus

16.000MPa

Strength

200MPa

Impact

85kJ/m²

AKROMID® B3 GF 50 6 black (20028) is a 50% glass fibre reinforced, inorganic high temperature stabilised polyamide 6 with very high stiffness and strength

128293080

AKROMID®

UL

NEXT S3 GF 30 1 HU black (8825)PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 black (8825) is a partially biobased and heat-stabilised PA6.10. With 30% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength and stiffness. This sustainable and UL listed grade is characterised by its low moisture absorption and high chemical resistance compared to classic PA6 and PA 6.6.

Features

Bio-based
heat stabilised 130
reduced moisture

Regulatory

ul

Properties

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

Sustainability

Biobased carbon content

59 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8600 MPa
6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,5 %
7,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Standard bending strength RP 3,5

ISO 178

2mm/min | d.a.m.
5,5 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
100 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
17 kJ/m²
12 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
195 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
145 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,31 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 - 1,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,8 - 1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more