Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROTEK®

PK-VM M 10 natural (7575)

PK

AKROTEK® PK-VM M 10 natural (7575) - Polyketon, 10 % mineral reinforced Tribology, friction and wear, chemical resistance, isotropic shrinkage

Modulus

2.900MPa

Strength

58MPa

Impact

50kJ/m²

AKROTEK® PK-VM M 10 natural (7575) - Polyketon, 10 % mineral reinforced Tribology, friction and wear, chemical resistance, isotropic shrinkage

PRECITE®

Preliminary

V GF 30 2 natural (7722)

PBT-ASA- GF 30

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

9.800MPa

Strength

140MPa

Impact

60kJ/m²

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

AKROMID®

Preliminary

C28 GF 25 FRT blue (7986)

PA-Blend

AKROMID® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

145MPa

Impact

60kJ/m²

AKROMID® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

AKROMID®

Preliminary

B25 GF 40 L black (8452)

PA6+PP GF40

AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.

Modulus

11.500MPa

Strength

150MPa

Impact

60kJ/m²

AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.

AKROMID®

Preliminary

NEXT B3 GF 30 1 L CR natural (8312)

PA6 + PP GF30

AKROMID® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/m²

AKROMID® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

AKROMID®

UL

B3 GF 40 1 HU black (8415)

PA6 GF40

AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.

AKROMID®

Preliminary

NEXT 5.10 3 GF 30 black (8467)

PA5.10 GF30

AKROMID® NEXT 5.10 3 GF 30 black (8467) - PA 5.10, 100% biobased, HMD-free, glass fibre reinforced, heat stabilised, high strength, E&E, automotive, sports and leisure, construction industry.

Modulus

8.300MPa

Strength

160MPa

Impact

72kJ/m²

AKROMID® NEXT 5.10 3 GF 30 black (8467) - PA 5.10, 100% biobased, HMD-free, glass fibre reinforced, heat stabilised, high strength, E&E, automotive, sports and leisure, construction industry.

128293080

AKROMID®

B3 GF 30 1 PST black (6647)PA6 GF30

AKROMID® B3 GF 30 1 PST schwarz (6647) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and optimized for adhesion to PST (Plasma Seal-Tight®) coatings developed by Plasmatreat®

Features

heat stabilised 130
adhesion modified

Properties

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10300 MPa
6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
270 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
95 kJ/m²
105 kJ/m²
85 kJ/m²
85 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
13 kJ/m²
18 kJ/m²
12 kJ/m²
12 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,16 10⁻⁴/K
0,95 10⁻⁴/K

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 - 2,3 %

Water absorption

ISO 62

23°C, saturated
6,3 - 6,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more