AKROMID®
NEXT B3 GF 30 1 L CR black (8313)
PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/m²
AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMID®
C28 GF 25 FRT grey (8331)
PA-Blend
AKROMID® C28 GF 25 FRT grey (8331) - PA blend, 25% glass fiber, flame retardant, good flowability, NCS S3000N, Public Transportation EN 45545-2.
10.800MPa
140MPa
47kJ/m²
AKROMID® C28 GF 25 FRT grey (8331) - PA blend, 25% glass fiber, flame retardant, good flowability, NCS S3000N, Public Transportation EN 45545-2.
AKROMID®
B25 GF 40 L black (8452)
PA6+PP GF40
AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.
11.500MPa
150MPa
60kJ/m²
AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.
PRECITE®
P3 GF 30 9 FR black (8424)
PBT GF30 FR(40)
PRECITE® P3 GF 30 9 FR black (8424) - PBT, 30% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.
10.500MPa
122MPa
50kJ/m²
PRECITE® P3 GF 30 9 FR black (8424) - PBT, 30% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.
AKROMID®
NEXT B3 GF 30 1 L CR natural (8312)
PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/m²
AKROMID® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMID®
C28 GF 25 FRT grey (8133)
PA-Blend
AKROMID® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.
11.000MPa
150MPa
NA
AKROMID® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.
AKROMID®
B3 GF 40 1 HU black (8415)
PA6 GF40
AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.
12.800MPa
205MPa
100kJ/m²
AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.
AKROMID®
B3 9 natural (6409)PA6
AKROMID® B3 9 natural (6409) is an unreinforced polyamide 6 with good flowability and very good demoulding properties. It is suitable for applications in the furniture industry, the sport and leisure as well as the automotive industry.
Features
Properties
3.300MPa
85MPa
Na
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at yield
ISO 527-2
Tensile strain at yield
ISO 527-2
Tensile strain at break
ISO 527-2
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.