PRECITE®

Preliminary

P3 GF 30 9 FR black (8424)

PBT GF30 FR(40)

PRECITE® P3 GF 30 9 FR black (8424) - PBT, 30% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

Modulus

10.500MPa

Strength

122MPa

Impact

50kJ/m²

PRECITE® P3 GF 30 9 FR black (8424) - PBT, 30% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

PRECITE®

Preliminary

E GF 15 ECO black (8327)

E GF 15 ECO

PRECITE® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

6.300MPa

Strength

110MPa

Impact

35kJ/m²

PRECITE® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITE®

Preliminary

P3 GF 15 4 natural (8429)

PBT-I GF15

PRECITE®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

Modulus

5.000MPa

Strength

85MPa

Impact

55kJ/m²

PRECITE®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

AKROMID®

A3 GF 35 2 black (21010)

PA66 GF35

AKROMID® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

Modulus

12.000MPa

Strength

185MPa

Impact

50kJ/m²

AKROMID® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

AKROMID®

UL

A3 GF 30 FR orange (7871)

PA66 GF30 FR(40)

AKROMID® A3 GF 30 FR orange (7871) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors. This material is coloured similar RAL2003

Modulus

10.400MPa

Strength

140MPa

Impact

60kJ/m²

AKROMID® A3 GF 30 FR orange (7871) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors. This material is coloured similar RAL2003

AKROMID®

Preliminary

T5 GF 35 6 natural (8005)

PPA GF35

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/m²

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

AKROMID®

B3 ICF 15 black (5026)

PA6 CF15

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

128293080

AKROMID®

A3 1 L black (4652)PA66 + PP

AKROMID® A3 1 L black (4652) is an unreinforced PA6.6/PP-blend with reduced density compared to standard PA6.6. The material can be used where weight and cost reduction is required.

Features

heat stabilised 130
reduced density

Properties

Modulus

2.300MPa

Strength

54MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
1300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
54 MPa
40 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
30 %
> 50 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
6,5 kJ/m²
12 kJ/m²
5 kJ/m²
4 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
65 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
800 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,04 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
2,5 %
1,8 %

Rheological Properties

MVR

ISO 1133

275°C/5kg
29 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more