AKROLOY®
PARA FGF 50 1 black (8186)
PARA FGF50
AKROLOY® PARA FGF 50 1 black (8186) - polyarylamide, 50% flat glass fiber reinforced, improved properties 90° to the flow direction, easy flowing
19.000MPa
295MPa
75kJ/m²
AKROLOY® PARA FGF 50 1 black (8186) - polyarylamide, 50% flat glass fiber reinforced, improved properties 90° to the flow direction, easy flowing
AKROMID®
B3 GF 60 4 RM-M natural (4645)
PA6 + X GF60
AKROMID® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.
21.500MPa
235MPa
65kJ/m²
AKROMID® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.
AKROLOY®
PA ICF 30 black (5269)
PA66+PA6I/6T CF30
AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
25.000MPa
220MPa
50kJ/m²
AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROMID®
A3 GF 50 HU grey (6601)
PA66 GF50
AKROMID® A3 GF 50 HU grey (6601) - 50% glass fiber reinforced PA 6.6, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and automotive industry
17.000MPa
255MPa
110kJ/m²
AKROMID® A3 GF 50 HU grey (6601) - 50% glass fiber reinforced PA 6.6, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and automotive industry
AKROMID®
A3 1 S3 black (21002)
PA66-I
AKROMID® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
2.300MPa
60MPa
180kJ/m²
AKROMID® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
PRECITE®
P3 GK 30 natural (7643)
PBT GK30
PRECITE® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.
3.900MPa
50MPa
25kJ/m²
PRECITE® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.
PRECITE®
E GF 35 natural (7626)
PET GF 35
PRECITE® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.
12.600MPa
180MPa
55kJ/m²
PRECITE® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.
AKROMID®
B3 GF 15 S3 black (2345)PA6-I GF15
AKROMID® B3 GF 15 S3 black (2345) is a 15% glass fiber reinforced, impact modified Polyamide 6. It is characterised by medium stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 15. It also has good surface properties. The material is therefore perfectly suitable for toughness demanding but high integrated parts with a good surface appearance in the automotive, electro, and furniture industry.
Features
Properties
5.500MPa
110MPa
75kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.