HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITE®

Preliminary

P3 8 natural (7517)

PBT

PRECITE® P3 8 natural (7517) - PBT, unreinforced, food contact, medium viscosity, good dimensional stability, FDA, EU10/2011, cosmetic, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE® P3 8 natural (7517) - PBT, unreinforced, food contact, medium viscosity, good dimensional stability, FDA, EU10/2011, cosmetic, E&E, appliances industries.

PRECITE®

Preliminary

K GF 50 8 black (8446)

PBT+PET GF50

PRECITE® K GF 50 8 black (8446) - PBT/PET blend, 50% glass fibre, very high strength, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

Modulus

17.500MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® K GF 50 8 black (8446) - PBT/PET blend, 50% glass fibre, very high strength, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

AKROMID®

Preliminary

B28 GM 10/20 6 black (8640)

PA6 (GF10+GB20)

B28 GM 10/20 6 black (8640) - PA 6 with 10% glass fibers and 20% glass beads reinforced, easy flowing with good surface properties.

Modulus

5.500MPa

Strength

100MPa

Impact

50kJ/m²

B28 GM 10/20 6 black (8640) - PA 6 with 10% glass fibers and 20% glass beads reinforced, easy flowing with good surface properties.

PRECITE®

Preliminary

E GF 20 8 black (7849)

PET GF 20 8

PRECITE® E GF 20 8 black (7849) - PET, 20% glass fibre, high stiffness, high toughness, dimensional stability, chemical resistance, food contact, very good surface, kitchen and household appliances.

Modulus

7.800MPa

Strength

NA

Impact

35kJ/m²

PRECITE® E GF 20 8 black (7849) - PET, 20% glass fibre, high stiffness, high toughness, dimensional stability, chemical resistance, food contact, very good surface, kitchen and household appliances.

AKROMID®

Preliminary

B3 GF 50 6 black (20028)

PA6 GF50

AKROMID® B3 GF 50 6 black (20028) is a 50% glass fibre reinforced, inorganic high temperature stabilised polyamide 6 with very high stiffness and strength

Modulus

16.000MPa

Strength

200MPa

Impact

85kJ/m²

AKROMID® B3 GF 50 6 black (20028) is a 50% glass fibre reinforced, inorganic high temperature stabilised polyamide 6 with very high stiffness and strength

AKROMID®

Preliminary

NEXT B3 GF 30 1 L CR black (8313)

PA6 + PP GF30

AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/m²

AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

AKROMID®

Preliminary

T5 GF 50 9 black (8001)

PPA GF50

AKROMID® T5 GF 50 9 black (8001) is a 50% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up. This product was optimized and provides a very good surface quality.

Modulus

18.500MPa

Strength

255MPa

Impact

65kJ/m²

AKROMID® T5 GF 50 9 black (8001) is a 50% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up. This product was optimized and provides a very good surface quality.

124252680

AKROMID®

A3 5 black (4701)PA66

AKROMID® A3 5 black (4701) is an unreinforced, high temperature stabilised polyamide 6.6

Features

heat stabilised 160

Properties

Modulus

3.500MPa

Strength

90MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3500 MPa
1450 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
90 MPa
55 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
4,5 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
12 %
≥ 30 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
125 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
≥ 4,5 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
V-2 Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,14 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more