PRECITE®

Preliminary

P3 GF 30 LA black (6969)

PBT GF 30

PRECITE® P3 GF 30 LA black (6969) is a 30% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and toughness as well as high dimensional and chemical resistance, laser markable.

Modulus

10.000MPa

Strength

145MPa

Impact

68kJ/m²

PRECITE® P3 GF 30 LA black (6969) is a 30% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and toughness as well as high dimensional and chemical resistance, laser markable.

AKROMID®

B28 GF 15 2 black (7060)

PA6 GF15

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/m²

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

PRECITE®

Preliminary

E GF 50 natural (7300)

PET GF50

PRECITE® E GF 50 natural (7300) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

18.100MPa

Strength

220MPa

Impact

70kJ/m²

PRECITE® E GF 50 natural (7300) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

A3 GF 30 4 6 black (13690)

PA66 GF30

AKROMID® A3 GF 30 4 6 black (13690) - PA6.6, 30% glass fiber, cooling water, hydrolysis resistant, DPPD free

Modulus

10.000MPa

Strength

190MPa

Impact

85kJ/m²

AKROMID® A3 GF 30 4 6 black (13690) - PA6.6, 30% glass fiber, cooling water, hydrolysis resistant, DPPD free

AKROMID®

C28 GFM 10/20 5 XTC black (7367)

PA66+PA6 (GF10+MD20)

AKROMID® C28 GFM 10/20 5 XTC black (7367) - 10% glass fiber and 20% mineral reinforced, easy flowing and high heat stabilised, high dimensional stability

Modulus

9.500MPa

Strength

120MPa

Impact

40kJ/m²

AKROMID® C28 GFM 10/20 5 XTC black (7367) - 10% glass fiber and 20% mineral reinforced, easy flowing and high heat stabilised, high dimensional stability

PRECITE®

Preliminary

P1 GF 30 natural (7062)

PBT GF30

PRECITE® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

9.800MPa

Strength

150MPa

Impact

75kJ/m²

PRECITE® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

PRECITE®

Preliminary

E GF 35 natural (7626)

PET GF 35

PRECITE® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

12.600MPa

Strength

180MPa

Impact

55kJ/m²

PRECITE® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

123242580

AKROMID®

UL

B3 1 black (6528)PA6

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Features

heat stabilised 130

Regulatory

ul

Properties

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3600 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
85 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
20 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
120 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
5 kJ/m²
16 kJ/m²
2 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
100 - 140 °C
90 - 120 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
V-2 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
3 PLC
3 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
1 PLC
1 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,13 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 3,4 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

UL
Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more