PRECITEĀ®

Preliminary

E ICF 30 black (7429)

PET CF30

PRECITEĀ® E ICF 30 black (7429) - PET, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

24.000MPa

Strength

220MPa

Impact

44kJ/mĀ²

PRECITEĀ® E ICF 30 black (7429) - PET, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

AKROTEKĀ®

PK-VM M 10 natural (7575)

PK

AKROTEKĀ® PK-VM M 10 natural (7575) - Polyketon, 10 % mineral reinforced Tribology, friction and wear, chemical resistance, isotropic shrinkage

Modulus

2.900MPa

Strength

58MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM M 10 natural (7575) - Polyketon, 10 % mineral reinforced Tribology, friction and wear, chemical resistance, isotropic shrinkage

PRECITEĀ®

Preliminary

P3 GF 50 7 natural (7866)

PBT GF 50

PRECITEĀ® P3 GF 50 7 natur (7866) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

15.800MPa

Strength

165MPa

Impact

75kJ/mĀ²

PRECITEĀ® P3 GF 50 7 natur (7866) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROMIDĀ®

A3 GF 35 2 black (21010)

PA66 GF35

AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

Modulus

12.000MPa

Strength

185MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

AKROMIDĀ®

B3 ICF 30 AM black (7451)

PA6 CF30

AKROMIDĀ® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.

Modulus

20.000MPa

Strength

190MPa

Impact

45kJ/mĀ²

AKROMIDĀ® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.

AKROMIDĀ®

A3 1 S3 natural (2847)

PA66-I

AKROMIDĀ® A3 1 S3 natural (2847) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 1 S3 natural (2847) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROMIDĀ®

C3 GF 30 1 black (4363)

PA66+PA6 GF30

AKROMIDĀ® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/mĀ²

AKROMIDĀ® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

122232480

AKROMIDĀ®

B3 GF 45 1 black (5744)PA6 GF45

AKROMIDĀ® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Properties

Modulus

14.000MPa

Strength

200MPa

Impact

110kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
14000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
13000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
315 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
4,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
110 kJ/mĀ²
95 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
22 kJ/mĀ²
18 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,5 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,45 - 0,65 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more