PRECITE®

Preliminary

P3 GK 30 natural (7643)

PBT GK30

PRECITE® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

Modulus

3.900MPa

Strength

50MPa

Impact

25kJ/m²

PRECITE® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

PRECITE®

Preliminary

E GF 35 natural (7626)

PET GF 35

PRECITE® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

12.600MPa

Strength

180MPa

Impact

55kJ/m²

PRECITE® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITE®

Preliminary

V GF 20 2 black (7738)

PBT-ASA- GF 20

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

6.500MPa

Strength

110MPa

Impact

50kJ/m²

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITE®

P3 GF 20 black (7609)

PBT GF20

PRECITE® P3 GF 20 schwarz (7609) - PBT, glass fibre reinforced, higher CTI and very good dimensional stability.

Modulus

7.000MPa

Strength

120MPa

Impact

50kJ/m²

PRECITE® P3 GF 20 schwarz (7609) - PBT, glass fibre reinforced, higher CTI and very good dimensional stability.

AKROMID®

A3 CF 30 5 black (7488)

PA66 CF30

AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

Modulus

26.000MPa

Strength

285MPa

Impact

90kJ/m²

AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

PRECITE®

V GF 30 2 black (7724)

PBT+ASA GF30

PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

Modulus

9.500MPa

Strength

130MPa

Impact

60kJ/m²

PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

PRECITE®

Preliminary

V GF 30 2 natural (7722)

PBT-ASA- GF 30

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

9.800MPa

Strength

140MPa

Impact

60kJ/m²

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

122232480

AKROMID®

A3 1 S3 black (21002)PA66-I

AKROMID® A3 1 S3 black (21002) is an unreinforced, impact modified Polyamide 66. It is characterised by a medium dry impact strength and good surface quality. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry.

Features

heat stabilised 130
impact modified
surface modified

Properties

Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
800 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
60 MPa
40 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
45 %
> 200 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2500 MPa
1000 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
16 kJ/m²
100 kJ/m²
12 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.