AKROMIDĀ®

B28 GF 30 S3 white (8349)

PA6-I GF30

AKROMIDĀ® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

Modulus

8.900MPa

Strength

150MPa

Impact

94kJ/mĀ²

AKROMIDĀ® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

AKROMIDĀ®

B3 GF 30 1 L black (4365)

PA6+PP GF30

AKROMIDĀ® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

Modulus

8.800MPa

Strength

140MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

AKROMIDĀ®

B28 GF 50 natural (4842)

PA6 GF50

AKROMIDĀ® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

Modulus

16.500MPa

Strength

250MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

AKROMIDĀ®

C3 GF 35 5 XTC black (6680)

PA66+PA6 GF35

AKROMIDĀ® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking

Modulus

11.500MPa

Strength

200MPa

Impact

105kJ/mĀ²

AKROMIDĀ® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking

AKROMIDĀ®

B3 GF 30 1 PST black (6647)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 PST schwarz (6647) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and optimized for adhesion to PST (Plasma Seal-TightĀ®) coatings developed by PlasmatreatĀ®

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 PST schwarz (6647) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and optimized for adhesion to PST (Plasma Seal-TightĀ®) coatings developed by PlasmatreatĀ®

AKROMIDĀ®

B28 GF 33 1 GIT black (6846)

PA6 GF33

AKROMIDĀ® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.

Modulus

10.500MPa

Strength

190MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.

PRECITEĀ®

Preliminary

P3 GF 50 black (6925)

PBT GF 50

PRECITEĀ® P3 GF 50 black (6925) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

17.000MPa

Strength

175MPa

Impact

60kJ/mĀ²

PRECITEĀ® P3 GF 50 black (6925) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

121222380

AKROMIDĀ®

B3 GF 50 black (4907)PA6 GF50

AKROMIDĀ® B3 GF 50 black (4907) is a 50% glass fibre reinforced high-flow polyamide 6 with very high rigidity and strength. The material is suitable for technical components in mechanical engineering, automotive industry as well as construction industry.

Features

easy flow

Properties

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17000 MPa
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
240 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
16000 MPa
11000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
360 MPa
250 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
100 kJ/mĀ²
105 kJ/mĀ²
90 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
20 kJ/mĀ²
23 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
185 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,11 10ā»ā“/K
0,94 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
150 - 165 Ā°C
120 - 140 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,56 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,6 %

Water absorption

ISO 62

23Ā°C, saturated
4,5 - 5,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
550 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more