Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

Preliminary

T5 GF 30 6 black (8006)

PPA GF30

AKROMIDĀ® T5 GF 30 black (8006) is a 30% glass fibre reinforced polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

11.800MPa

Strength

200MPa

Impact

45kJ/mĀ²

AKROMIDĀ® T5 GF 30 black (8006) is a 30% glass fibre reinforced polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

AKROMIDĀ®

Preliminary

C28 GF 25 FRT blue (7986)

PA-Blend

AKROMIDĀ® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

145MPa

Impact

60kJ/mĀ²

AKROMIDĀ® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

AKROMIDĀ®

B3 GF 45 1 black (5744)

PA6 GF45

AKROMIDĀ® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.000MPa

Strength

200MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

AKROMIDĀ®

C3 GF 35 5 XTC black (6680)

PA66+PA6 GF35

AKROMIDĀ® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking

Modulus

11.500MPa

Strength

200MPa

Impact

105kJ/mĀ²

AKROMIDĀ® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking

PRECITEĀ®

Preliminary

P3 ICF 10 black (6946)

PBT CF10

PRECITEĀ® P3 ICF 10 black (6946) - PBT, 10% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

7.500MPa

Strength

100MPa

Impact

30kJ/mĀ²

PRECITEĀ® P3 ICF 10 black (6946) - PBT, 10% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

PRECITEĀ®

Preliminary

E GF 30 natural (7303)

PET GF 30

PRECITEĀ® E GF 30 natural (7303) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

10.600MPa

Strength

175MPa

Impact

48kJ/mĀ²

PRECITEĀ® E GF 30 natural (7303) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMIDĀ®

A3 1 S3 black (21002)

PA66-I

AKROMIDĀ® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

121222380

AKROMIDĀ®

B3 GF 50 S1 black (2000)PA6-I GF50

AKROMIDĀ® B3 GF 50 S1 black 950089 (2000) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. The material is therefore perfectly suitable for industrial applications and for housings and covers in the automotive industry.

Features

impact modified

Properties

Modulus

15.000MPa

Strength

190MPa

Impact

100kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
15000 MPa
7800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
190 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
8 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
100 kJ/mĀ²
> 110 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
25 kJ/mĀ²
40 kJ/mĀ²
20 kJ/mĀ²
20 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,54 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.