Select your fitting and find the right compound for your intend
AKROMID®
B28 GF 30 S3 white (8349)
PA6-I GF30
AKROMID® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry
8.900MPa
150MPa
94kJ/m²
AKROMID® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry
AKROMID®
NEXT B3 GF 30 1 L CR black (8313)
PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/m²
AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMID®
B25 GF 40 L black (8452)
PA6+PP GF40
AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.
11.500MPa
150MPa
60kJ/m²
AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.
AKROMID®
B3 GF 50 1 black (2488)
PA6 GF50
AKROMID® B3 GF 50 1 black (2488) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
17.000MPa
230MPa
100kJ/m²
AKROMID® B3 GF 50 1 black (2488) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GF 30 S1 LA black (4446)
PA6-I GF30
AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive
8.400MPa
150MPa
110kJ/m²
AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive
AKROLOY®
PA GF 60 natural (6465)
PA66+PA6I/6T GF60
AKROLOY® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
21.000MPa
280MPa
100kJ/m²
AKROLOY® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROMID®
T5 GF 40 black (6486)
PPA GF40
AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
14.500MPa
245MPa
80kJ/m²
AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
AKROTEK®
AKROTEK® PK-VM GF 10 LT schwarz (8652) is a 10% glass fibre reinforced polyketone compound with average stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. The compound can be welded via laser welding and the corresponding laserabsorbing PK-VM GF 10 black (8685). This type was developed as the successor to PK-VM GF 10 LT black (8290) and PK-VM GF 10 LT black (8529) in order to meet the requirements for a larger processing window during processing.
Features
Properties
3.500MPa
80MPa
55kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 75
ISO 11357-3
UL 94
ISO 1183
ISO 1110
ISO 294-4
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.