Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

B28 GF 15 2 black (7060)

PA6 GF15

AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/mĀ²

AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

AKROMIDĀ®

A3 1 S3 black (21002)

PA66-I

AKROMIDĀ® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

PRECITEĀ®

Preliminary

P1 GF 30 natural (7062)

PBT GF30

PRECITEĀ® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

9.800MPa

Strength

150MPa

Impact

75kJ/mĀ²

PRECITEĀ® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

PRECITEĀ®

Preliminary

E GF 35 natural (7626)

PET GF 35

PRECITEĀ® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

12.600MPa

Strength

180MPa

Impact

55kJ/mĀ²

PRECITEĀ® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMIDĀ®

A3 GF 35 2 black (21010)

PA66 GF35

AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

Modulus

12.000MPa

Strength

185MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

AKROMIDĀ®

C28 GF 25 FRT grey (7560)

PA-Blend

AKROMIDĀ® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

135MPa

Impact

60kJ/mĀ²

AKROMIDĀ® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

AKROMIDĀ®

Preliminary

B3 GF 50 6 black (20028)

PA6 GF50

AKROMIDĀ® B3 GF 50 6 black (20028) is a 50% glass fibre reinforced, inorganic high temperature stabilised polyamide 6 with very high stiffness and strength

Modulus

16.000MPa

Strength

200MPa

Impact

85kJ/mĀ²

AKROMIDĀ® B3 GF 50 6 black (20028) is a 50% glass fibre reinforced, inorganic high temperature stabilised polyamide 6 with very high stiffness and strength

118192080

PRECITEĀ®

Preliminary

P3 GF 30 4 black (8333)PBT-I GF30

PRECITEĀ® P3 GF 30 4 black (8333) is a 30% glass fibre reinforced and hydrolysis stabilised polybutylene terephthalate (PBT). It is characterised by a high stiffness and toughness as well as good chemical resistance. This formulation is GMA free (glycidyl methacrylate) and meets the VW-50136 standard. Furthermore, the material impresses with very good dimensional stability due to its low moisture absorption. Therefore, the material is perfectly suitable for technical precision components in applications in the automotive industry, mechanical engineering, E&E and household goods industries with increased humidity.

Features

hydrolysis / chemically stabilised
impact modified
low warpage
reduced moisture
E&E
Sports & leisure

Properties

Modulus

9.000MPa

Strength

115MPa

Impact

65kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
9000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
115 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
65 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
13 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23Ā°C
1,48 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,8 - 1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.