Find the right compound
Select your fitting and find the right compound for your intend
AKROMIDĀ®
A3 GF 50 HU grey (6601)
PA66 GF50
AKROMIDĀ® A3 GF 50 HU grey (6601) - 50% glass fiber reinforced PA 6.6, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and automotive industry
17.000MPa
255MPa
110kJ/mĀ²
AKROMIDĀ® A3 GF 50 HU grey (6601) - 50% glass fiber reinforced PA 6.6, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
B28 GF 15 2 black (7060)
PA6 GF15
AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.
6.100MPa
108MPa
32kJ/mĀ²
AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.
AKROMIDĀ®
B3 GFM 20/30 1 black (7677)
PA6 (GF20+MD30)
AKROMIDĀ® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.
14.000MPa
145MPa
45kJ/mĀ²
AKROMIDĀ® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.
AKROMIDĀ®
A3 GF 35 2 black (21010)
PA66 GF35
AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength
12.000MPa
185MPa
50kJ/mĀ²
AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength
AKROMIDĀ®
B3 ICF 30 AM black (7451)
PA6 CF30
AKROMIDĀ® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
20.000MPa
190MPa
45kJ/mĀ²
AKROMIDĀ® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
AKROMIDĀ®
NEXT B3 GF 30 1 L CR natural (8312)
PA6 + PP GF30
AKROMIDĀ® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/mĀ²
AKROMIDĀ® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMIDĀ®
B3 GF 15 1 L black (4670)
PA6+PP GF15
AKROMIDĀ® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride
5.200MPa
105MPa
60kJ/mĀ²
AKROMIDĀ® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride
AKROMIDĀ®
B3 GF 30 1 black (20000)PA6 GF30
AKROMIDĀ® B3 GF 30 1 black (20000) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering as well as in the automotive and agricultural machinery industry.
Features
Properties
9.500MPa
175MPa
90kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Ball indentation hardness
ISO 2039-1
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.