PRECITEĀ®
V GF 20 2 natural (7737)
PBT-ASA- GF 20
PRECITE V GF 20 2 natural (7737) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.
6.500MPa
110MPa
50kJ/mĀ²
PRECITE V GF 20 2 natural (7737) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.
PRECITEĀ®
P3 GF 50 7 natural (7866)
PBT GF 50
PRECITEĀ® P3 GF 50 7 natur (7866) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.
15.800MPa
165MPa
75kJ/mĀ²
PRECITEĀ® P3 GF 50 7 natur (7866) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.
AKROMIDĀ®
B3 ICF 40 AM black (8236)
PA6 CF40
AKROMIDĀ® B3 ICF 40 AM black (8236) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
27.000MPa
210MPa
45kJ/mĀ²
AKROMIDĀ® B3 ICF 40 AM black (8236) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
AKROMIDĀ®
C28 GF 25 FRT grey (8133)
PA-Blend
AKROMIDĀ® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.
11.000MPa
150MPa
NA
AKROMIDĀ® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.
AKROMIDĀ®
NEXT B3 GF 30 1 L CR natural (8312)
PA6 + PP GF30
AKROMIDĀ® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/mĀ²
AKROMIDĀ® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMIDĀ®
B28 GF 15 2 black (7060)
PA6 GF15
AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.
6.100MPa
108MPa
32kJ/mĀ²
AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.
AKROMIDĀ®
A3 1 S3 black (21002)
PA66-I
AKROMIDĀ® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
2.300MPa
60MPa
180kJ/mĀ²
AKROMIDĀ® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
AKROMIDĀ®
B3 GK 30 black (1827)PA6 GB30
AKROMIDĀ® B3 GK 30 black (1827) is a PA 6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.
Features
Properties
4.500MPa
75MPa
20kJ/mĀ²
Sustainability
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Ball indentation hardness
ISO 2039-1
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Temperature index for 50% loss of tensile strength
IEC 60216
Vicat softening temperature B50
ISO 306
Flammability
Burning rate
UL 94
GWIT
IEC 60695-2-13
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Rheological Properties
Flowability
AKRO
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.