AKROMID®
C28 GF 25 FRT natural (7332)
PA-Blend
C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.
10.800MPa
157MPa
64kJ/m²
C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.
AKROMID®
B3 GFM 15/25 black (1312)
PA6 (GF15+MD25)
AKROMID® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability
8.000MPa
120MPa
50kJ/m²
AKROMID® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability
AKROMID®
A3 GF 40 1 black (2386)
PA66 GF40
AKROMID® A3 GF 40 1 black (2386) - 40% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
13.100MPa
225MPa
100kJ/m²
AKROMID® A3 GF 40 1 black (2386) - 40% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GK 30 black (1827)
PA6 GB30
AKROMID® B3 GK 30 black (1827) - PA 6, 30% glass beads reinforced, good surface, low warpage
4.500MPa
75MPa
20kJ/m²
AKROMID® B3 GK 30 black (1827) - PA 6, 30% glass beads reinforced, good surface, low warpage
AKROMID®
A3 GF 30 1 black (2385)
PA66 GF30
AKROMID® A3 GF 30 1 black (2385) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry
10.000MPa
200MPa
85kJ/m²
AKROMID® A3 GF 30 1 black (2385) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry
AKROMID®
B3 GF 30 natural (2472)
PA6 GF30
AKROMID® B3 GF 30 natural (2472) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
10.300MPa
185MPa
95kJ/m²
AKROMID® B3 GF 30 natural (2472) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
AKROMID®
A3 GF 30 1 natural (2391)
PA66 GF30
AKROMID® A3 GF 30 1 natural (2391) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry
10.000MPa
200MPa
85kJ/m²
AKROMID® A3 GF 30 1 natural (2391) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry
AKROMID®
NEXT 5.6 3 GF 30 natural (8405)PA5.6 GF30
AKROMID® NEXT 5.6 3 GF 30 natur (8405) is a HMD-free (hexamethylenediamine) alternative to PA 6.6. The partly bio-based material with 30% glass fibre is suitable for parts with high demands on stiffness and strength.
Features
Properties
9.500MPa
185MPa
66kJ/m²
Sustainability
Biobased carbon content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.