AKROMID®
T9 GF 50 black (7601)
PPA GF50
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROTEK®
RA GFM 15/25 black (8216)
PA6 (GF15+MD25)
AKROTEK® RA GFM 15/25 black (8216) - PA 6, 15% glass fiber reinforced, 25% mineral filled, radar absorption, 76-81 GHz
8.500MPa
120MPa
50kJ/m²
AKROTEK® RA GFM 15/25 black (8216) - PA 6, 15% glass fiber reinforced, 25% mineral filled, radar absorption, 76-81 GHz
AKROMID®
NEXT 5.6 3 GF 30 FR black (8465)
PA56 GF30 FR(40)
AKROMID® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.
11.000MPa
137MPa
64kJ/m²
AKROMID® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.
AKROLOY®
PARA GF 35 FR black (7496)
PARA GF35 FR(40)
AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
14.500MPa
190MPa
55kJ/m²
AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
AKROLOY®
PARA GF 50 HU natural (8595)
PARA GF50
AKROLOY® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute
19.000MPa
310MPa
80kJ/m²
AKROLOY® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute
AKROMID®
D3 GF 30 1 black (5392)
PA612 GF30
AKROMID® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector
9.500MPa
180MPa
95kJ/m²
AKROMID® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector
AKROLOY®
PA GF 50 natural (6414)
PA66+PA6I/6T GF50
AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
17.000MPa
275MPa
110kJ/m²
AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
AKROMID®
NEXT B3 GF 30 1 L CI black (8375)PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) is a PA6/PP-blend with reduced density compared to standard PA6 GF 30. With 30% glass fibre reinforcement, the material is suitable for components with high strength and stiffness where weight reduction are required. The chemical resistance is particularly superior to calcium chloride (CaCl₂). The material is certified according to ISCC PLUS. 34% of the fossil raw materials required for manufacturing this product were replaced by sustainable biomass-balanced PP (≙ allocation factor).
Features
Regulatory
Properties
8.800MPa
140MPa
70kJ/m²
Sustainability
Allocation factor
only valid for ISCC PLUS/REDcert² certified products
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Ball indentation hardness
ISO 2039-1
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.