Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

B3 GF 30 6 black (20009)

PA6 GF30

AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

180MPa

Impact

80kJ/m²

AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

D3 GF 30 1 black (5392)

PA612 GF30

AKROMID® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector

Modulus

9.500MPa

Strength

180MPa

Impact

95kJ/m²

AKROMID® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector

PRECITE®

P3 GFM 20/10 natural (7627)

PBT (GF20+MD10)

PRECITE® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/m²

PRECITE® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

AKROLOY®

Preliminary

PARA GF 35 FR orange (8039)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

AKROLOY®

Preliminary

PARA GF 35 FR grey (8200)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

AKROLOY®

PARA GF 35 FR black (7496)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

55kJ/m²

AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

AKROLOY®

Preliminary

PARA GF 35 FR natural (8038)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

110111280

AKROMID®

Preliminary

NEXT U3 ICF 20 1 black (8232)PA11 CF20

AKROMID® NEXT U3 ICF 20 1 black (8232) is a Polyamide 11 reinforced with 20% recycled carbon fibre. The PA 11 is made from castor seed oil (bio-based content > 92%). The compound's low density as well as excellent ductility even at lower temperatures combined with high stiffness and strength enable the use for demanding applications, e.g., for lightweight construction or sports & leisure. Furthermore, the material is suitable for Fused Filament Fabrication (FFF) for further processing in additive manufacturing.

Features

heat stabilised 130
recycled content
reduced density
reduced moisture
3D printing / additive manufacturing
Sports & leisure
lightweight construction

Properties

Modulus

9.300MPa

Strength

110MPa

Impact

60kJ/m²

Sustainability

Biobased carbon content

63 %

Recycled content

20 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9300 MPa
7300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
110 MPa
90 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5,1 %
4,7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
9100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
110 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
15 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
189 °C

General properties

Density

ISO 1183

23°C
1,12 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 - 0,9 %

Water absorption

ISO 62

23°C, saturated
1,3 - 1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more