PA6 – Polyamide 6 PA6 CF 15 + GF 20

AKROMID® B3 CGM 15/20 1 LA black (8058)

AKROMID® B3 CGM 15/20 1 LA black (8058) is a 15% carbon fibre reinforced, 20% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength. Furthermore, the material impresses with its good laser marking properties as well as electrical conductivity. It is therefore perfectly suitable for technical applications in the automotive industry e.g. fuel filter housing.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

heat stabilised 130
laser markable
sustainable
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 17000 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 195 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,5 %

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 70 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 10 kJ/m²

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 210 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 220 °C

    Coefficent of linear thermal expansion, parallel (23°C bis 80°C | ISO 11359-1/2) 0,07 1,0E-4/K

    Coefficent of linear thermal expansion, transverse (23°C bis 80°C | ISO 11359-1/2) 0,98 1,0E-4/K

  • Flammability

    Burning rate (UL 94)
    1,6mm Wall thickness HB Class

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties

    Density (23°C | ISO 1183) 1,36 g/cm³

    Molding shrinkage (flow | ISO 294-4) 0,1-0,3 %

    Molding shrinkage (transverse | ISO 294-4) 0,5-0,7 %

  • Electrical Properties

    Surface resistivity (DIN EN 62631-3-2) d.a.m. 1,0E+4 Ω

  • Sustainability

    Recycled content (at least) 15 %

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 240 - 290°C

3 Nozzle temperature 260 - 300°C

4 Melt temperature 270 - 290°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.