PET – Polyethyleneterephthalate PET CF30
PRECITE® E ICF 30 black (7429)PRECITE® E ICF 30 black (7429) is medium viscosity polyethylene terephthalate (PET) with 30% recycled carbon fiber. Despite lower density compared to PET with glass fiber reinforcement, the product has very high strength and toughness as well as high dimensional stability. The good tribological properties and improved surface finish make it the material of choice for precision components in the automotive, mechanical engineering, E&E and household goods industries.
Properties
Tensile Modulus Tensile Strength Impact StrengthFeatures
-
Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 24000 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 220 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 1,9 %
Flexural modulus (2 mm/min | ISO 178) d.a.m. 24500 MPa
Flexural strength (2 mm/min | ISO 178) d.a.m. 325 MPa
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 44 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 6 kJ/m²
-
Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 215 °C
Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 250 °C
Coefficent of linear thermal expansion, parallel (23°C bis 80°C | ISO 11359-1/2) 0,05 1,0E-4/K
Coefficent of linear thermal expansion, transverse (23°C bis 80°C | ISO 11359-1/2) 0,73 1,0E-4/K
-
Flammability
Burning rate (UL 94) 0,8mm Wall thickness HB Class
-
General properties
Density (23°C | ISO 1183) 1,45 g/cm³
Humidity absorption (70°C, 62% r.H. | ISO 1110) 0,1-0,3 %
Molding shrinkage (flow | ISO 294-4) 0,1 - 0,3 %
Molding shrinkage (transverse | ISO 294-4) 0,5 - 0,7 %
-
Electrical Properties
Volume resistivity (DIN EN 62631-3-1) d.a.m. <1,0E+3 Ω · cm
Surface resistivity (DIN EN 62631-3-2) d.a.m. <1,0E+3 Ω
-
Sustainability
Recycled content (at least) 30 %
Processing information
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
 |
Drying time | 3 - 4 h |
| Drying temperature (τ ≤ -30°C) | 120 - 140°C | |
| Processing moisture | ≤ 0,02% | |
 |
Feed section | 60 - 80°C |
 |
Temperature zone 1 - Zone 4 | 270 - 290°C |
 |
Nozzle temperature | 270 - 295°C |
 |
Melt temperature | 270 - 290°C |
 |
Mold temperature | 130 - 160°C |
 |
Holding pressure, spec. | 300 - 800 bar |
 |
Back pressure, spec. | 30 - 100 bar |
| Injection speed | medium to high | |
| Screw speed | 8 - 15 m/min | |
Warning
Due to hydrolysis sensitivity of polyesters, a careful drying of the material before processing is very important. High residual moisture contents causes, in addition to surface defects, a decomposition of the molecular chains and thus reduced mechanical properties. If there are longer interruptions of the process, the cylinder temperature should be lowered. Furthermore, we recommend a thorough cleaning of the screw cylinder with extended dwell time or a material change. Glass-fiber-reinforced polyolefins (PE, PP) have established a particularly good cleaning effect.
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.