Menu Career Language: EN/DE
keyboard_arrow_left pdf Download

PA6 – Polyamide 6 PA6 GF60

AKROMID® B3 GF 60 1 black (4644)

21000 MPa

  • 21000 MPa

  • 13500 MPa

250 MPa

  • 250 MPa

  • 160 MPa

90 kJ/m²

  • 90 kJ/m²

  • 95 kJ/m²

  • 90 kJ/m²

AKROMID® B3 GF 60 1 black (4644) is a 60% glass fibre reinforced, heat stabilised and easy flowing polyamide 6 with very high rigidity and strength

Typical applications

Components in mechanical engineering and in the automotive industry

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
6 Drying time 0 - 4 h
Drying temperature (τ ≤ -30°C) 80°C
Processing moisture 0,02 - 0,1%
1 Feed section 60 - 80°C
2 Temperature zone 1 - Zone 4 240 - 290°C
3 Nozzle temperature 260 - 300°C
4 Melt temperature 270 - 290°C
5 Mold temperature 80 - 100°C
P Nach Holding pressure, spec. 300 - 800 bar
P Stau Back pressure, spec. 50 - 150 bar
Injection speed medium to high
Screw speed 8 - 15 m/min
  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 21000 MPa
    conditioned 13500 MPa
    Stress at break (5 mm/min | ISO 527-2)
    d.a.m. 250 MPa
    conditioned 160 MPa
    Strain at break (5 mm/min | ISO 527-2)
    d.a.m. 2,5 %
    conditioned 3,5 %
    Flexural modulus (2 mm/min | ISO 178)
    d.a.m. 19000 MPa
    Flexural strength (2 mm/min | ISO 178)
    d.a.m. 370 MPa
    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m. 90 kJ/m²
    conditioned 95 kJ/m²
    Charpy impact strength (-30°C | ISO 179-1/1eU)
    d.a.m. 90 kJ/m²
    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m. 20 kJ/m²
    conditioned 25 kJ/m²
    Charpy notched impact strength (-30°C | ISO 179-1/1eA)
    d.a.m. 20 kJ/m²
  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 220 °C
    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 220 °C
    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 220 °C
    Coefficent of linear thermal expansion, parallel (23°C bis 80°C | ISO 11359-1/2) 0,13 1,0E-4/K
    Coefficent of linear thermal expansion, transverse (23°C bis 80°C | ISO 11359-1/2) 0,60 1,0E-4/K
  • Flammability
    Burning rate (UL 94)
    0,8mm Wall thickness HB Class
    GWFI (IEC 60695-2-12)
    1,6mm Wall thickness 650 °C
    GWIT (IEC 60695-2-13)
    1,6mm Wall thickness 675 °C
    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
  • General properties
    Density (23°C | ISO 1183) 1,7 g/cm³
    Humidity absorption (70°C, 62% r.H. | ISO 1110) 0,9 - 1,2 %
    Molding shrinkage (flow | ISO 294-4) 0,1 - 0,3 %
    Molding shrinkage (transverse | ISO 294-4) 0,3 - 0,5 %
  • Rheological Properties
    Flowability (2mm Thickness | AKRO) 320 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.