AKROMID®

A3 GF 15 1 GIT black (4620)PA66 GF15

AKROMID® A3 GF 15 1 GIT black (4620) is a 15% glass fibre reinforced, heat stabilised, easy flowing polyamide 6.6. It is characterised by average stiffness and strength and shows an excellent surface. Furthermore, the material is designed for gas injection technology.

Features

heat stabilised 130
surface modified
fluid injection (GIT/WIT/FIT)

Properties

Modulus

5.500MPa

Strength

125MPa

Impact

40kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
5500 MPa
3500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
125 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
12 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
40 kJ/m²
75 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
7 kJ/m²
8 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,9 - 1,1 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.