PA GF 50 grey (3807)PA66 + PA6I/6T GF50

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

Properties

Modulus

17.200MPa

Strength

250MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17200 MPa
16500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,7 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
13200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
360 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
105 kJ/m²
100 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
16 kJ/m²
17 kJ/m²
15 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
221 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
245 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,59 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 %
0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.