PA6.10 – Polyamide 6.10 PA610 GF50
AKROMID® S3 GF 50 1 black (3441)
AKROMID® S3 GF 50 1 black (3441) is a 50% glass fibre reinforced and heat stabilised polyamide 6.10 with very high stiffness and strength as well as lower moisture absorption and high chemical resistance.
Precision parts for apparatus engineering and precision mechanics as well as connectors, housings etc. in the automotive industry.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||240 - 290°C|
|Nozzle temperature||240 - 300°C|
|Melting temperature||270 - 290°C|
|Mold temperature||80 - 100°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
- Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 14500 MPa conditioned 11000 MPa Stress at break (5 mm/min | ISO 527-2) d.a.m. 200 MPa conditioned 150 MPa Strain at break (5 mm/min | ISO 527-2) d.a.m. 3,5 % conditioned 4,5 % Flexural modulus (2 mm/min | ISO 178) d.a.m. 13800 MPa Flexural strength (2 mm/min | ISO 178) d.a.m. 310 MPa Flexural strain at break (2 mm/min | ISO 178) d.a.m. 3,6 % Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 100 kJ/m² conditioned 100 kJ/m² Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 105 kJ/m² Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 20 kJ/m² Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 16 kJ/m² Ball indentation hardness (961N/30s | ISO 2039-1) d.a.m. 230 MPa
- Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 205 °C Temperature of deflection under load HDT/C (8 MPa | ISO 75) 170 °C Melting temperature (DSC, 10K/min | DIN EN 11357-1) 220 °C
Burning rate (UL 94) 0,8mm Wall thickness HB Class Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
- General properties
Density (23°C | ISO 1183) 1,51 g/cm³ Humidity absorption (70°C, 62% r.F. | ISO 1110) 0,9 % Molding shrinkage (flow | ISO 294-4) 0,1-0,3 % Molding shrinkage (transverse | ISO 294-4) 0,6-0,8 %
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.