PA6.6 – Polyamide 6.6 PA66-I
AKROMID® A3 S1 black (1071)
AKROMID® A3 S1 black 950089 (1071) is an unreinforced, cold impact modified polyamide 6.6
Typical applications
Connectors and fixtures for the automotive electro and furniture industry, if high impact resistance at low temperatures is required.
Processing information
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
 | Drying time | 0 - 4 h |
| Drying temperature (τ ≤ -30°C) | 80°C | |
| Processing moisture | 0,02 - 0,1% | |
 | Feed section | 60 - 80°C |
 | Temperature zone 1 - Zone 4 | 260 - 300°C |
 | Nozzle temperature | 270 - 310°C |
 | Melting temperature | 280 - 300°C |
 | Mold temperature | 40 - 80°C |
 | Holding pressure, spec. | 300 - 800 bar |
 | Back pressure, spec. | 50 - 150 bar |
| Injection speed | medium to high | |
| Screw speed | 8 - 15 m/min | |
- Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 2000 MPa conditioned 900 MPa Stress at yield (50 mm/min | ISO 527-2) d.a.m. 50 MPa conditioned 40 MPa Strain at yield (50 mm/min | ISO 527-2) d.a.m. 4,8 % Strain at break (50 mm/min | ISO 527-2) d.a.m. > 50 % conditioned > 100 % Flexural modulus (2 mm/min | ISO 178) d.a.m. 1950 MPa Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. n.b. kJ/m² conditioned n.b. kJ/m² Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. o.B. kJ/m² conditioned o.B. kJ/m² Charpy impact strength (-40°C | ISO 179-1/1eU) d.a.m. o.B. kJ/m² Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. > 80 kJ/m² conditioned > 100 kJ/m² Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 35 kJ/m² conditioned 35 kJ/m² Charpy notched impact strength (-40°C | ISO 179-1/1eA) d.a.m. 35 kJ/m² Ball indentation hardness (358N/30s | ISO 2039-1) d.a.m. 80 MPa - Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 70 °C Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 152 °C Melting temperature (DSC, 10K/min | DIN EN 11357-1) 262 °C - Flammability
Burning rate (UL 94) 1,6mm Wall thickness HB Class Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) + - General properties
Density (23°C | ISO 1183) 1,07 g/cm³ Humidity absorption (70°C, 62% r.F. | ISO 1110) 2,0 % Molding shrinkage (flow | ISO 294-4) 1,3 - 1,5 % Molding shrinkage (transverse | ISO 294-4) 1,5 - 1,7 % - Electrical Properties
Volume resistivity (IEC 60093) d.a.m. 1,0E+15 Ohm x cm Surface resistivity (acc. to IEC 60093) d.a.m. 1,0E+14 Ohm Comparative tracking index (Test liquid A | IEC 60112) 600 V
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.