PRECITE®
P3 GF 30 4 7 LA black (8304)
PBT-I GF30
PRECITE®P3 GF 30 4 7 LA black (8304) is a 30% glass fibre reinforced, hydrolysis stabilised polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance. This formulation is free of GMA and fulfills VW-50136 standard.
Features
Properties
8.800MPa
115MPa
70kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Flammability
Burning rate
UL 94
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Processing information
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problem and surface defects.
Drying time
3 - 4 h
Drying temperature (τ ≤ -30°C)
100 - 120 °C
Processing moisture
0,02 - 0,04 %
Feed section
60 - 80 °C
Temperature Zone 1 - Zone 4
250 - 275 °C
Nozzle temperature
250 - 280 °C
Melt temperature
260 - 275 °C
Mold temperature
80 - 100 °C
Holding pressure, spec.
300 - 800 bar
Back pressure, spec.
30 - 100 bar
Injection speed
medium to high
Screw speed
8 - 15 m/min
Applications
Explore more exciting application examples that illustrate how our products can be beneficial to you in various situations and industries.
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.