Deutsch

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa

Tensile Strengthin MPa

Charpy impact strengthin kJ/m²

AKROMID

394

PRECITE

AKROTEK

AKROLOY

AKROLEN

AKROMID

PA6.6

109

PA6

199

PA6.6/6

PPA

PA11

PA5.6

PA5.10

PA6.9

PA6.10

PA6.12

AKROLOY

PARA

PA6.6/PA6I-6T

PRECITE

PBT

PET

PBT/PET

AKROTEK

AKROLEN

Sustainability

recycled content

biomass balanced

Bio-based

Stabilisation

heat stabilised 130

189

heat stabilised 160

heat stabilised 230

hydrolysis / chemically stabilised

UV-stabilised

electrically neutral

Modification

flame retardant

impact modified

laser markable

laser transparent

surface modified

low warpage

reduced density

reduced moisture

antistatic/conductive

adhesion modified

tribological modified

Processing

easy flow

process improved

fluid injection (GIT/WIT/FIT)

3D printing / additive manufacturing

nucleated

Special Application Field

E&E

public transportation

lightweight construction

metal substitution

Sports & leisure

radar applications

E-Mobility

glass fibre

388

unreinforced

carbon fibre

glass bead

glass fibre/glass bead

glass fibre/mineral

long glass fibre

mineral

glass fibre/carbon fibre

554 Compounds found

Recommended

Tensile Modulus

Tensile Strength

Charpy impact strength

Description

AKROMID^®

NEXT S3 GF 30 1 HU black (8825)

PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

1 77 78 7980

AKROTEK^®

Preliminary

Internal

PK-VM GF 30 LT black (8653)PK GF30

AKROTEK® PK-VM GF 30 LT black (8653) is a 30% glass fibre reinforced, lasertransparent low viscous polyketone with high stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. This type was developed as the successor to PK-VM GF 30 LT black (8530) und PK-VM GF 30 LT black (6934) in order to meet the requirements for a larger processing window during processing.

Features

hydrolysis / chemically stabilised

laser transparent

Properties

Modulus

8.300MPa

Strength

130MPa

Impact

65kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

8300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

130 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

2,6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

8200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

210 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

15 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

215 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

220 °C

General properties

Density

ISO 1183

23°C

1,48 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

0,6 - 0,7 %

Molding shrinkage

ISO 294-4

flow

transverse

0,3 - 0,5 %

0,8 - 1,0 %

Rheological Properties

MVR

ISO 1133

240°C/2,16kg

4 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.