Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
554 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROTEK®

Preliminary

PK-VM GF 15 black (8686)

PK GF15

AKROTEK® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

4.500MPa

Strength

90MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

UL
Preliminary

C3 GF 30 1 FR natural (7207)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR natural (7207) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

Modulus

10.500MPa

Strength

150MPa

Impact

76kJ/m²

AKROMID® C3 GF 30 1 FR natural (7207) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

AKROMID®

UL

C3 GF 30 1 FR black (7243)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR black (7243) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

Modulus

10.800MPa

Strength

148MPa

Impact

74kJ/m²

AKROMID® C3 GF 30 1 FR black (7243) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

AKROMID®

UL
Preliminary

B28 GF 35 9 FR orange (8573)

PA6 GF35 FR(40)

AKROMID® B28 GF 35 9 FR orange (8573) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

Modulus

12.600MPa

Strength

145MPa

Impact

60kJ/m²

AKROMID® B28 GF 35 9 FR orange (8573) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

AKROMID®

UL

C3 GF 25 1 FR black (7246)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

Modulus

9.100MPa

Strength

137MPa

Impact

66kJ/m²

AKROMID® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

AKROLOY®

UL

PA GF 50 HU black (8198)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 HU black (8198) is an UL listed, 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

17.000MPa

Strength

265MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 HU black (8198) is an UL listed, 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMID®

UL
Preliminary

C3 GF 30 1 FR grey (8384)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR grey (8384) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 7035, E&E, Public transportation EN 45545-2.

Modulus

10.000MPa

Strength

121MPa

Impact

46kJ/m²

AKROMID® C3 GF 30 1 FR grey (8384) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 7035, E&E, Public transportation EN 45545-2.

123480

AKROMID®

Preliminary

A3 GF 30 6 ECO black (8160)PA6.6 GF30

AKROMID® A3 GF 30 6 ECO black (8160) is a 30% glass fibre-reinforced, inorganically heat-stabilised polyamide 6.6. The material is suitable for technical components in mechanical engineering and the automotive industry with demands for high stiffness and strength. The formulations of the sustainable ECO products are partly based on regenerated post-industrial feedstock (at least 30 weight-% by recipe) and thus contribute to reducing the consumption of valuable raw materials. This type is laser-markable.

Features

recycled content
heat stabilised 160
laser markable

Properties

Modulus

9.000MPa

Strength

150MPa

Impact

50kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9000 MPa
6300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
150 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7500 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
50 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
7 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.