Deutsch

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa

Tensile Strengthin MPa

Charpy impact strengthin kJ/m²

AKROMID

394

PRECITE

AKROTEK

AKROLOY

AKROLEN

AKROMID

PA6.6

109

PA6

199

PA6.6/6

PPA

PA11

PA5.6

PA5.10

PA6.9

PA6.10

PA6.12

AKROLOY

PARA

PA6.6/PA6I-6T

PRECITE

PBT

PET

PBT/PET

AKROTEK

AKROLEN

Sustainability

recycled content

biomass balanced

Bio-based

Stabilisation

heat stabilised 130

189

heat stabilised 160

heat stabilised 230

hydrolysis / chemically stabilised

UV-stabilised

electrically neutral

Modification

flame retardant

impact modified

laser markable

laser transparent

surface modified

low warpage

reduced density

reduced moisture

antistatic/conductive

adhesion modified

tribological modified

Processing

easy flow

process improved

fluid injection (GIT/WIT/FIT)

3D printing / additive manufacturing

nucleated

Special Application Field

E&E

public transportation

lightweight construction

metal substitution

Sports & leisure

radar applications

E-Mobility

glass fibre

388

unreinforced

carbon fibre

glass bead

glass fibre/glass bead

glass fibre/mineral

long glass fibre

mineral

glass fibre/carbon fibre

554 Compounds found

Recommended

Tensile Modulus

Tensile Strength

Charpy impact strength

Description

AKROMID^®

NEXT S3 GF 30 1 HU black (8825)

PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

1 77 78 7980

AKROMID^®

Preliminary

T9 GF 50 black (7601)PPA GF50

AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Features

heat stabilised 160

Properties

Modulus

17.000MPa

Strength

250MPa

Impact

95kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

17000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

250 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

2,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

30°C | d.a.m.

95 kJ/m²

80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

30°C | d.a.m.

16 kJ/m²

14 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min

305 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness

HB Class

General properties

Density

ISO 1183

23°C

1,55 g/cm³

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A

600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.