AKROMID®

Preliminary

T5 GF 50 6 black (8000)

PPA GF50

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up


Modulus

18.500MPa

Strength

260MPa

Impact

65kJ/m²

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up

AKROMID®

UL

A3 GF 30 HU natural (6661)

PA66 GF30

AKROMID® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry


Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry

AKROMID®

UL
Preliminary

C3 GF 25 1 FR orange (7854)

PA66/6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR orange (7854) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, RAL 2003, automotive, E&E.


Modulus

9.000MPa

Strength

126MPa

Impact

61kJ/m²

AKROMID® C3 GF 25 1 FR orange (7854) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, RAL 2003, automotive, E&E.

AKROTEK®

Preliminary

PK-VM GF 15 black (8686)

PK GF15

AKROTEK® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance


Modulus

4.500MPa

Strength

90MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance

PRECITE®

Preliminary

K GF 30 4 LA ECO black (8699)

PBT-PET- GF 30

PRECITE® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.


Modulus

9.500MPa

Strength

120MPa

Impact

65kJ/m²

PRECITE® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR orange (8537)

PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.


Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.

AKROMID®

UL
Preliminary

B28 GF 30 9 FR orange (8645)

PA6 GF30 FR(40)

AKROMID® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.


Modulus

10.200MPa

Strength

138MPa

Impact

70kJ/m²

AKROMID® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

123480

AKROMID®

Internal

B3 GF 30 4 L black (7481)PA6 + PP GF30

AKROMID® B3 GF 30 4 L black (7481) is a PA6/PP-blend with reduced density compared to standard PA6 with 30% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMID® B3 GF 30 4 L black (7481) is particularly superior to water glycol. This compound fulfills the requirements of VW TL52682 (1000h/135°C; 50/50 G12 EVO/water) and can be used for applications that are in contact witch cooling water.

Features

heat stabilised 130
hydrolysis / chemically stabilised
reduced density

Properties

Modulus

9.000MPa

Strength

145MPa

Impact

70kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9000 MPa
7000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
145 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,1 %
4,6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
9200 MPa
6500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
225 MPa
160 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,4 %
4,3 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
70 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
17 kJ/m²
18 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
170 MPa

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,17 10⁻⁴/K
1,34 10⁻⁴/K

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,26 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties


MVR

ISO 1133

275°C/5kg
14 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.