AKROMID®

Preliminary

NEXT B28 GF 30 9 FR black (8342BMBCI)

PA6 GF30 FR(40)

AKROMID® NEXT B28 GF 30 9 FR schwarz (8342BMBCI) - PA6, 30% glass fibre, sustainable, biomass-balanced, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

148MPa

Impact

75kJ/m²

AKROMID® NEXT B28 GF 30 9 FR schwarz (8342BMBCI) - PA6, 30% glass fibre, sustainable, biomass-balanced, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, V0 from 1,6 mm, e-mobility.

AKROMID®

UL

NEXT S3 GF 30 1 HU natural (8824)

PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 natural (8824) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 1 natural (8824) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMID®

UL

NEXT S3 GF 30 1 HU black (8825)

PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROTEK®

Preliminary

PK-VM GF 30 8 black (8783)

PK GF30

AKROTEK® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

Modulus

8.100MPa

Strength

130MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

AKROMID®

UL

NEXT S3 GF 50 1 HU black (8827)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 black (8827) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 50 1 black (8827) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMID®

UL

C3 GF 25 1 FR grey (8605)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

Modulus

9.100MPa

Strength

125MPa

Impact

50kJ/m²

AKROMID® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

AKROMID®

UL

NEXT S3 GF 50 1 HU natural (8826)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 natural (8826) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 50 1 natural (8826) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

177787980

AKROMID®

B28 GF 15 2 black (7060)PA6 GF15

AKROMID® B28 GF 15 2 black (7060) is a 15% glass fiber reinforced, easy-flowing polyamide 6. It is characterized by medium rigidity and strength. In addition, the material is heat and UV stabilized and therefore ideally suited for technical components in outdoor applications. This product passed ISO 4892-2 with 1200h exposure time.

Features

heat stabilised 160
UV-stabilised

Properties

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
6100 MPa
3300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
108 MPa
70 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,0 %
9 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
32 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Flammability

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 2,9 %

Water absorption

ISO 62

23°C, saturated
7,7 - 8,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.