PRECITE®

Preliminary

K GF 30 4 LA ECO black (8699)

PBT-PET- GF 30

PRECITE® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.


Modulus

9.500MPa

Strength

120MPa

Impact

65kJ/m²

PRECITE® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROLOY®

UL

PA GF 50 HU black (8198)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 HU black (8198) is an UL listed, 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.


Modulus

17.000MPa

Strength

265MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 HU black (8198) is an UL listed, 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMID®

UL

C3 GF 25 1 FR natural (7208)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR natural (7208) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.


Modulus

9.200MPa

Strength

140MPa

Impact

73kJ/m²

AKROMID® C3 GF 25 1 FR natural (7208) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

AKROMID®

UL

C3 GF 30 1 FR black (7243)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR black (7243) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.


Modulus

10.800MPa

Strength

148MPa

Impact

74kJ/m²

AKROMID® C3 GF 30 1 FR black (7243) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

AKROMID®

UL

C3 GF 25 1 FR black (7246)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.


Modulus

9.100MPa

Strength

137MPa

Impact

66kJ/m²

AKROMID® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

AKROMID®

UL

C3 GF 30 1 FR white (7630)

PA6+PA66 GF30 FR(40)

AKROMID® C3 GF 30 1 FR white (7630) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 9016, E&E, Public transportation EN 45545-2.


Modulus

10.600MPa

Strength

140MPa

Impact

NA

AKROMID® C3 GF 30 1 FR white (7630) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 9016, E&E, Public transportation EN 45545-2.

AKROMID®

UL
Preliminary

C3 GF 30 1 FR natural (7207)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR natural (7207) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.


Modulus

10.500MPa

Strength

150MPa

Impact

76kJ/m²

AKROMID® C3 GF 30 1 FR natural (7207) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

123480

AKROTEK®

Preliminary

PK-VM GF 10 8 natural (6981)PK GF10

AKROTEK® PK-VM GF 10 8 natural (6981) is a 10% glass fibre reinforced polyketone with average stiffness and strength. PK is characterized by its outstanding media resistance, which qualifies it to be used for components that are in contact with chemicals. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances. Please note that the material is NOT suitable anymore for drinking water contact and does NOT meet the requirements according to KTW, DVGW W270, ACS, WRAS as well as NSF61.

Features

hydrolysis / chemically stabilised

Regulatory

eu102011fda

Properties

Modulus

3.700MPa

Strength

80MPa

Impact

50kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3700 MPa
3600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
80 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,2 %
4,2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
50 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
9 kJ/m²
9 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,32 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 - 0,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,7 - 0,9 %
1,3 - 1,5 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more