Deutsch

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa

Tensile Strengthin MPa

Charpy impact strengthin kJ/m²

AKROMID

394

PRECITE

AKROTEK

AKROLOY

AKROLEN

AKROMID

PA6.6

109

PA6

199

PA6.6/6

PPA

PA11

PA5.6

PA5.10

PA6.9

PA6.10

PA6.12

AKROLOY

PARA

PA6.6/PA6I-6T

PRECITE

PBT

PET

PBT/PET

AKROTEK

AKROLEN

Sustainability

recycled content

biomass balanced

Bio-based

Stabilisation

heat stabilised 130

189

heat stabilised 160

heat stabilised 230

hydrolysis / chemically stabilised

UV-stabilised

electrically neutral

Modification

flame retardant

impact modified

laser markable

laser transparent

surface modified

low warpage

reduced density

reduced moisture

antistatic/conductive

adhesion modified

tribological modified

Processing

easy flow

process improved

fluid injection (GIT/WIT/FIT)

3D printing / additive manufacturing

nucleated

Special Application Field

E&E

public transportation

lightweight construction

metal substitution

Sports & leisure

radar applications

E-Mobility

glass fibre

388

unreinforced

carbon fibre

glass bead

glass fibre/glass bead

glass fibre/mineral

long glass fibre

mineral

glass fibre/carbon fibre

554 Compounds found

Recommended

Tensile Modulus

Tensile Strength

Charpy impact strength

Description

AKROMID^®

NEXT S3 GF 30 1 HU black (8825)

PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

1 77 78 7980

AKROMID^®

A3 GF 30 6 black (6736)PA66 GF30

AKROMID® A3 GF 30 6 black (6736) is a 30% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is anorganically heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry which are exposed to higher temperatures.

Features

heat stabilised 160

Properties

Modulus

10.000MPa

Strength

200MPa

Impact

75kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

10000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

3,2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

75 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

255 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

262 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h

165 °C

Flammability

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

1,9 - 2,1 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.