Description

PRECITE®

Preliminary

P3 GF 30 4 LA black (8286)

PBT-I GF30

PRECITE®P3 GF 30 4 LA black (8286) is a 30% glass fibre reinforced, hydrolysis stabilised and lasermarkable polybutylene terephthalate (PBT). It is characterised by a high stiffness and toughness as well as good chemical resistance. This formulation is GMA free (glycidyl methacrylate) and meets the VW-50136 standard. Furthermore, the material impresses with very good dimensional stability due to its low moisture absorption. Therefore, the material is perfectly suitable for technical precision components in applications in the automotive industry, mechanical engineering, E&E and household goods industries with increased humidity.


Modulus

9.100MPa

Strength

120MPa

Impact

70kJ/m²

PRECITE®P3 GF 30 4 LA black (8286) is a 30% glass fibre reinforced, hydrolysis stabilised and lasermarkable polybutylene terephthalate (PBT). It is characterised by a high stiffness and toughness as well as good chemical resistance. This formulation is GMA free (glycidyl methacrylate) and meets the VW-50136 standard. Furthermore, the material impresses with very good dimensional stability due to its low moisture absorption. Therefore, the material is perfectly suitable for technical precision components in applications in the automotive industry, mechanical engineering, E&E and household goods industries with increased humidity.

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR natural (8448)

PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR natural (8448) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, process improved, good dimensional stability. high voltage components, e-mobility.


Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 FR natural (8448) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, process improved, good dimensional stability. high voltage components, e-mobility.

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR black (8604)

PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR black (8604) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, process improved, good dimensional stability. high voltage components, e-mobility, lasermarkable.


Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 FR black (8604) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, process improved, good dimensional stability. high voltage components, e-mobility, lasermarkable.

AKROMID®

UL
Preliminary

C3 GF 30 1 FR grey (8384)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR grey (8384) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 7035, E&E, Public transportation EN 45545-2.


Modulus

10.000MPa

Strength

121MPa

Impact

46kJ/m²

AKROMID® C3 GF 30 1 FR grey (8384) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 7035, E&E, Public transportation EN 45545-2.

AKROMID®

UL
Preliminary

B28 GF 35 9 FR orange (8573)

PA6 GF35 FR(40)

AKROMID® B28 GF 35 9 FR orange (8573) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.


Modulus

12.600MPa

Strength

145MPa

Impact

60kJ/m²

AKROMID® B28 GF 35 9 FR orange (8573) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

AKROMID®

Preliminary

A3 1 S3 black (11392)

PA66-I

AKROMID® A3 1 S3 black (11392) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, low emission


Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (11392) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, low emission

AKROMID®

Preliminary

T5 GF 50 6 natural (8056)

PPA GF50

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 natural (8056) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps its mechanical performance even at elevated temperatures or moisture pick-up


Modulus

18.000MPa

Strength

270MPa

Impact

90kJ/m²

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 natural (8056) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps its mechanical performance even at elevated temperatures or moisture pick-up

123480

AKROMID®

UL

A3 GF 30 HU natural (6661)PA66 GF30

AKROMID® A3 GF 30 HU natural (6661) is a 30% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry. Additionally, it is listed at UL in all colors. The material has a light inherent color.

Features

heat stabilised 130

Regulatory

ul

Properties

Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10500 MPa
7500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
130 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,1 %
6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
75 kJ/m²
83 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
12 kJ/m²
16 kJ/m²

UV Exposure and Water Immersion

UL 746C

UL
f2

Thermal Properties


RTI electrical

UL 746B

UL
0,4mm Wall thickness
UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
125 °C
125 °C
130 °C
130 °C

RTI impact

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
120 °C
120 °C
120 °C

RTI strength

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
130 °C
130 °C
130 °C

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
210 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
150 - 160 °C
120 - 130 °C

Flammability


Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
HB Class

HWI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
4 PLC
4 PLC
4 PLC

HAI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,35 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Electrical Properties


Volume resistivity IEC

DIN EN IEC 62631-3-2

UL
d.a.m.
1011 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Dielectric strength

IEC 60243

UL
3 mm
12 kV/mm

High voltage arc tracking rate (HVTR)

UL 746A

UL
5 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.