AKROMID®

B3 GF 35 1 natural (2465)

PA6 GF35

AKROMID® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 50 1 black (2387)

PA66 GF50

AKROMID® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

Preliminary

NEXT 5.10 3 GF 30 natural (8406)

PA5.10 GF30

AKROMID® NEXT 5.10 3 GF 30 natural (8406) - 100% biobased and HMD-free PA 5.10 with high strength.

Modulus

8.300MPa

Strength

160MPa

Impact

72kJ/m²

AKROMID® NEXT 5.10 3 GF 30 natural (8406) - 100% biobased and HMD-free PA 5.10 with high strength.

AKROMID®

B3 GF 50 4 RM-M black (3221)

PA6+X GF50

AKROMID® B3 GF 50 4 RM-M black (3221) - 50% glass fiber reinforced PA 6 with good surface properties, chemically stabilised, reduced moisture absorption

Modulus

16.500MPa

Strength

210MPa

Impact

75kJ/m²

AKROMID® B3 GF 50 4 RM-M black (3221) - 50% glass fiber reinforced PA 6 with good surface properties, chemically stabilised, reduced moisture absorption

AKROMID®

UL
Preliminary

B28 GF 25 9 FR natural (8066)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

8.900MPa

Strength

138MPa

Impact

83kJ/m²

AKROMID® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

PRECITE®

Preliminary

E GF 30 ECO black (8271)

PET GF30

PRECITE® E GF 30 ECO black (8271) - PET, 30% glass fiber, high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

Modulus

10.500MPa

Strength

170MPa

Impact

45kJ/m²

PRECITE® E GF 30 ECO black (8271) - PET, 30% glass fiber, high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

AKROMID®

B3 GF 30 1 natural (2464)

PA6 GF30

AKROMID® B3 GF 30 1 natural (2464) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 natural (2464) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

134580

AKROMID®

B3 ICF 15 black (5026)PA6 CF15

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

Properties

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
5000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
9000 MPa
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
200 MPa
150 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
55 kJ/m²
80 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
6 kJ/m²
10 kJ/m²
4 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,17 10⁻⁴/K
0,66 10⁻⁴/K

Thermal conductivity

DIN 52612

0,31 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,19 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,7 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
105 Ω
105 Ω

Rheological Properties

Flowability

AKRO

2 mm Thickness
360 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.