AKROMIDĀ®

UL

NEXT S3 GF 30 1 HU black (8825)

PA6.10 GF30

AKROMIDĀ® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/mĀ²

AKROMIDĀ® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

177787980

AKROMIDĀ®

B3 GF 30 1 L natural (4684)PA6+PP GF30

AKROMIDĀ® B3 GF 30 1 L natural (4684) is a PA6/PP-blend with reduced density compared to standard PA6 with 30% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 30 1 L natural (4684) is particularly superior to calcium chloride (CaClā‚‚).

Features

heat stabilised 130
reduced density

Properties

Modulus

8.500MPa

Strength

150MPa

Impact

70kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8500 MPa
6500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
150 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,2 %
3,7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
8800 MPa
6500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
210 MPa
150 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3 %
3,9 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
70 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
17 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
203 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,26 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

MVR

ISO 1133

275Ā°C/5kg
14 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more