AKROMID®

B3 GF 35 1 natural (2465)

PA6 GF35

AKROMID® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 50 1 black (2387)

PA66 GF50

AKROMID® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

PRECITE®

P3 S1 black (7522)

PBT I

PRECITE® P3 S1 black (7522) - PBT unreinforced, impact modified, good dimensional stability.

Modulus

1.750MPa

Strength

40MPa

Impact

180kJ/m²

PRECITE® P3 S1 black (7522) - PBT unreinforced, impact modified, good dimensional stability.

AKROMID®

B3 GF 30 1 natural (2464)

PA6 GF30

AKROMID® B3 GF 30 1 natural (2464) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 natural (2464) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 50 1 black (20008)

PA6 GF50

AKROMID® B3 GF 50 black (20008) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

210MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (20008) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

PRECITE®

Preliminary

K GF 30 ECO black (8269)

PBT+PET GF30

PRECITE® K GF 30 ECO black (8269) - PBT/PET blend, recycled PET content, 30% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

10.000MPa

Strength

150MPa

Impact

60kJ/m²

PRECITE® K GF 30 ECO black (8269) - PBT/PET blend, recycled PET content, 30% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROMID®

UL
Preliminary

B28 GF 25 9 FR natural (8066)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

8.900MPa

Strength

138MPa

Impact

83kJ/m²

AKROMID® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

134580

AKROMID®

A3 GF 30 4 black (3571)PA66 GF30

AKROMID® A3 GF 30 4 black (3571) is a 30% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is hydrolysis and chemically stabilised and therefore perfectly suitable for e.g. cooling systems in the automotive industry.

Features

hydrolysis / chemically stabilised

Properties

Modulus

11.500MPa

Strength

210MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11500 MPa
6800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
210 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
310 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
80 kJ/m²
100 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
12 kJ/m²
20 kJ/m²
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,37 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more