PRECITE®

Preliminary

K GF 30 4 LA ECO black (8699)

PBT-PET- GF 30

PRECITE® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.


Modulus

9.500MPa

Strength

120MPa

Impact

65kJ/m²

PRECITE® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROMID®

UL

C3 GF 25 1 FR black (7246)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.


Modulus

9.100MPa

Strength

137MPa

Impact

66kJ/m²

AKROMID® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

AKROMID®

UL

C3 GF 30 1 FR white (7630)

PA6+PA66 GF30 FR(40)

AKROMID® C3 GF 30 1 FR white (7630) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 9016, E&E, Public transportation EN 45545-2.


Modulus

10.600MPa

Strength

140MPa

Impact

NA

AKROMID® C3 GF 30 1 FR white (7630) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 9016, E&E, Public transportation EN 45545-2.

PRECITE®

Preliminary

P3 GF 30 4 LA black (8286)

PBT-I GF30

PRECITE®P3 GF 30 4 LA black (8286) is a 30% glass fibre reinforced, hydrolysis stabilised and lasermarkable polybutylene terephthalate (PBT). It is characterised by a high stiffness and toughness as well as good chemical resistance. This formulation is GMA free (glycidyl methacrylate) and meets the VW-50136 standard. Furthermore, the material impresses with very good dimensional stability due to its low moisture absorption. Therefore, the material is perfectly suitable for technical precision components in applications in the automotive industry, mechanical engineering, E&E and household goods industries with increased humidity.


Modulus

9.100MPa

Strength

120MPa

Impact

70kJ/m²

PRECITE®P3 GF 30 4 LA black (8286) is a 30% glass fibre reinforced, hydrolysis stabilised and lasermarkable polybutylene terephthalate (PBT). It is characterised by a high stiffness and toughness as well as good chemical resistance. This formulation is GMA free (glycidyl methacrylate) and meets the VW-50136 standard. Furthermore, the material impresses with very good dimensional stability due to its low moisture absorption. Therefore, the material is perfectly suitable for technical precision components in applications in the automotive industry, mechanical engineering, E&E and household goods industries with increased humidity.

AKROMID®

UL
Preliminary

C3 GF 30 1 FR grey (8384)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR grey (8384) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 7035, E&E, Public transportation EN 45545-2.


Modulus

10.000MPa

Strength

121MPa

Impact

46kJ/m²

AKROMID® C3 GF 30 1 FR grey (8384) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 7035, E&E, Public transportation EN 45545-2.

AKROMID®

UL

C3 GF 30 1 FR black (7243)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR black (7243) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.


Modulus

10.800MPa

Strength

148MPa

Impact

74kJ/m²

AKROMID® C3 GF 30 1 FR black (7243) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

AKROMID®

UL

C3 GF 25 1 FR natural (7208)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR natural (7208) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.


Modulus

9.200MPa

Strength

140MPa

Impact

73kJ/m²

AKROMID® C3 GF 25 1 FR natural (7208) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

123480

AKROMID®

B3 GF 35 1 natural (2465)PA6 GF35

AKROMID® B3 GF 35 1 natural (2465) is a 35% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry. The material has a light inherent color.

Features

heat stabilised 130

Properties

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11500 MPa
7300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
195 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
285 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
110 kJ/m²
90 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
15 kJ/m²
21 kJ/m²
13 kJ/m²

Izod impact strength

ISO 180/1A

23°C | d.a.m.
85 kJ/m²

Izod notched impact strength

ISO 180/1A

23°C | d.a.m.
20 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
240 MPa

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
165 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,41 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 - 2,1 %

Water absorption

ISO 62

23°C, saturated
5,9 - 6,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties


Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012
1010

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more