Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROLOYĀ®

Preliminary

PARA GF 35 FR grey (8200)

PARA GF35 FR(40)

AKROLOYĀ® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.


Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROLOYĀ® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

AKROMIDĀ®

B3 GF 30 6 black (20009)

PA6 GF30

AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry


Modulus

10.000MPa

Strength

180MPa

Impact

80kJ/mĀ²

AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

PRECITEĀ®

P3 GFM 20/10 natural (7627)

PBT (GF20+MD10)

PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.


Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

AKROMIDĀ®

Preliminary

T9 GF 50 black (7601)

PPA GF50

AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.


Modulus

17.000MPa

Strength

250MPa

Impact

95kJ/mĀ²

AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

AKROLOYĀ®

Preliminary

PARA GF 35 FR orange (8039)

PARA GF35 FR(40)

AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.


Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

AKROTEKĀ®

PK-VM natural (4774)

PK

AKROTEKĀ® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance


Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance

AKROLOYĀ®

PA GF 50 natural (6414)

PA66+PA6I/6T GF50

AKROLOYĀ® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.


Modulus

17.000MPa

Strength

275MPa

Impact

110kJ/mĀ²

AKROLOYĀ® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

1891080

AKROTEKĀ®

Preliminary
Internal

PK-VM GF 30 LT black (8653)PK GF30

AKROTEKĀ® PK-VM GF 30 LT black (8653) is a 30% glass fibre reinforced, lasertransparent low viscous polyketone with high stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. This type was developed as the successor to PK-VM GF 30 LT black (8530) und PK-VM GF 30 LT black (6934) in order to meet the requirements for a larger processing window during processing.

Features

hydrolysis / chemically stabilised
laser transparent

Properties

Modulus

8.300MPa

Strength

130MPa

Impact

65kJ/mĀ²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
130 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
210 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
65 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
15 kJ/mĀ²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

General properties


Density

ISO 1183

23Ā°C
1,48 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,6 - 0,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,8 - 1,0 %

Rheological Properties


MVR

ISO 1133

240Ā°C/2,16kg
4 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more