Find the right compound
Select your fitting and find the right compound for your intend
AKROLOYĀ®
PARA GF 35 FR grey (8200)
PARA GF35 FR(40)
AKROLOYĀ® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.
14.500MPa
190MPa
50kJ/mĀ²
AKROLOYĀ® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.
AKROMIDĀ®
B3 GF 30 6 black (20009)
PA6 GF30
AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
10.000MPa
180MPa
80kJ/mĀ²
AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
PRECITEĀ®
P3 GFM 20/10 natural (7627)
PBT (GF20+MD10)
PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.
9.300MPa
115MPa
50kJ/mĀ²
PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.
AKROMIDĀ®
T9 GF 50 black (7601)
PPA GF50
AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/mĀ²
AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLOYĀ®
PARA GF 35 FR orange (8039)
PARA GF35 FR(40)
AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.
14.500MPa
190MPa
50kJ/mĀ²
AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.
AKROTEKĀ®
PK-VM natural (4774)
PK
AKROTEKĀ® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance
1.500MPa
60MPa
180kJ/mĀ²
AKROTEKĀ® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance
AKROLOYĀ®
PA GF 50 natural (6414)
PA66+PA6I/6T GF50
AKROLOYĀ® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
17.000MPa
275MPa
110kJ/mĀ²
AKROLOYĀ® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
AKROMIDĀ®
A3 GF 30 HU natural (6661)PA66 GF30
AKROMIDĀ® A3 GF 30 HU natural (6661) is a 30% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry. Additionally, it is listed at UL in all colors. The material has a light inherent color.
Features
Regulatory
Properties
10.500MPa
200MPa
75kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
UV Exposure and Water Immersion
UL 746C
Thermal Properties
RTI electrical
UL 746B
RTI impact
UL 746B
RTI strength
UL 746B
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Temperature index for 50% loss of tensile strength
IEC 60216
Flammability
Burning rate
UL 94
HWI
UL 746A
HAI
UL 746A
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Dielectric strength
IEC 60243
High voltage arc tracking rate (HVTR)
UL 746A
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.