AKROMID®

Preliminary

NEXT B28 GF 30 9 FR black (8342BMBCI)

PA6 GF30 FR(40)

AKROMID® NEXT B28 GF 30 9 FR schwarz (8342BMBCI) - PA6, 30% glass fibre, sustainable, biomass-balanced, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

148MPa

Impact

75kJ/m²

AKROMID® NEXT B28 GF 30 9 FR schwarz (8342BMBCI) - PA6, 30% glass fibre, sustainable, biomass-balanced, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, V0 from 1,6 mm, e-mobility.

AKROMID®

UL

NEXT S3 GF 50 1 HU natural (8826)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 natural (8826) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 50 1 natural (8826) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMID®

Preliminary

B28 GF 15 1 grey (8857)

PA6 GF15

AKROMID® B28 GF 15 1 grey (8857) - PA6, 15% glass fiber, heat stabilised, easy flowing, grey, industrial engineering, automotive.

Modulus

6.200MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GF 15 1 grey (8857) - PA6, 15% glass fiber, heat stabilised, easy flowing, grey, industrial engineering, automotive.

PRECITE®

Preliminary

P3 GF 30 8 black (8639)

PBT GF30

PRECITE® P3 GF 30 8 black (8639) - PBT, 30% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

Modulus

10.000MPa

Strength

140MPa

Impact

60kJ/m²

PRECITE® P3 GF 30 8 black (8639) - PBT, 30% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

AKROMID®

NEXT B3 GF 30 1 black (2485BMBCI)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485BMBCI) - PA 6, 30 % glass fiber, heat stabilised, high stiffness and strength, sustainable, biomass-balanced, technical parts in industrial engineering and automotive industry.

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® B3 GF 30 1 black (2485BMBCI) - PA 6, 30 % glass fiber, heat stabilised, high stiffness and strength, sustainable, biomass-balanced, technical parts in industrial engineering and automotive industry.

177787980

AKROMID®

UL
Preliminary

B28 GF 25 9 FR orange (8644)PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR orange (8644) is a flame retardant PA6 with 25% glass fibres, colored in orange, similar to RAL 2003. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. This grade is UL listed with a V0 classification at 1.6mm. Due to its very good flowability, it is characterised by easy processability as well as good surface properties. The material has excellent long-term thermal stability and outstanding mechanical properties.

Features

heat stabilised 130
electrically neutral
flame retardant
easy flow
E&E
E-Mobility

Regulatory

ul

Properties

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9000 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
135 MPa
95 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,7 %
7,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
81 kJ/m²
83 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

UL
1,8 MPa
207 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
165 °C
135 °C

Flammability

Burning rate

UL 94

UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
960 °C

HWI

UL 746A

UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC

HAI

UL 746A

UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,38 g/cm³

Water absorption

ISO 62

23°C, saturated
2,1 - 2,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

UL
d.a.m.
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

UL
d.a.m.
1012 Ω

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Dielectric strength

IEC 60243

UL
3 mm
18 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

UL
1,5 kV

High voltage arc tracking rate (HVTR)

UL 746A

UL
1 PLC

High Volt, Low Current Arc Resistance

ASTM D495

UL
4 PLC

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
130 mm
410 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more