AKROMID®

Preliminary

NEXT B28 GF 30 9 FR black (8342BMBCI)

PA6 GF30 FR(40)

AKROMID® NEXT B28 GF 30 9 FR schwarz (8342BMBCI) - PA6, 30% glass fibre, sustainable, biomass-balanced, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

148MPa

Impact

75kJ/m²

AKROMID® NEXT B28 GF 30 9 FR schwarz (8342BMBCI) - PA6, 30% glass fibre, sustainable, biomass-balanced, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, V0 from 1,6 mm, e-mobility.

AKROMID®

UL

NEXT S3 GF 50 1 HU natural (8826)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 natural (8826) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 50 1 natural (8826) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMID®

Preliminary

B28 GF 15 1 grey (8857)

PA6 GF15

AKROMID® B28 GF 15 1 grey (8857) - PA6, 15% glass fiber, heat stabilised, easy flowing, grey, industrial engineering, automotive.

Modulus

6.200MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GF 15 1 grey (8857) - PA6, 15% glass fiber, heat stabilised, easy flowing, grey, industrial engineering, automotive.

PRECITE®

Preliminary

P3 GF 30 8 black (8639)

PBT GF30

PRECITE® P3 GF 30 8 black (8639) - PBT, 30% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

Modulus

10.000MPa

Strength

140MPa

Impact

60kJ/m²

PRECITE® P3 GF 30 8 black (8639) - PBT, 30% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

AKROMID®

NEXT B3 GF 30 1 black (2485BMBCI)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485BMBCI) - PA 6, 30 % glass fiber, heat stabilised, high stiffness and strength, sustainable, biomass-balanced, technical parts in industrial engineering and automotive industry.

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® B3 GF 30 1 black (2485BMBCI) - PA 6, 30 % glass fiber, heat stabilised, high stiffness and strength, sustainable, biomass-balanced, technical parts in industrial engineering and automotive industry.

177787980

AKROMID®

A3 S3 natural (1176)PA66-I

AKROMID® A3 S3 natural (1176) is an unreinforced, dry impact modified Polyamide 6.6. The material is characterised by a very high impact strength and therefore perfectly suitable for connecting and fixing systems which are used in the automotive and electro industry and that are exposed to high loading speeds. The material has a light inherent color.

Features

impact modified

Properties

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2800 MPa
1700 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
67 MPa
45 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
6 %
26 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 30 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2850 MPa
1600 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
17 kJ/m²
95 kJ/m²
8 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
93 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
67 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
213 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
263 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 %

Molding shrinkage

ISO 294-4

flow
transverse
1,8 %
2,1 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1014 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more