AKROMID®

UL

NEXT S3 GF 30 1 HU black (8825)

PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMID®

UL

NEXT S3 GF 50 1 HU black (8827)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 black (8827) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 50 1 black (8827) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMID®

Preliminary

B28 GF 15 1 grey (8857)

PA6 GF15

AKROMID® B28 GF 15 1 grey (8857) - PA6, 15% glass fiber, heat stabilised, easy flowing, grey, industrial engineering, automotive.

Modulus

6.200MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GF 15 1 grey (8857) - PA6, 15% glass fiber, heat stabilised, easy flowing, grey, industrial engineering, automotive.

PRECITE®

Preliminary

P3 GF 30 8 black (8639)

PBT GF30

PRECITE® P3 GF 30 8 black (8639) - PBT, 30% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

Modulus

10.000MPa

Strength

140MPa

Impact

60kJ/m²

PRECITE® P3 GF 30 8 black (8639) - PBT, 30% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

AKROMID®

UL

C3 GF 25 1 FR grey (8605)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

Modulus

9.100MPa

Strength

125MPa

Impact

50kJ/m²

AKROMID® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

AKROMID®

UL

NEXT S3 GF 50 1 HU natural (8826)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 natural (8826) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 50 1 natural (8826) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROTEK®

Preliminary

PK-VM GF 30 8 black (8783)

PK GF30

AKROTEK® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

Modulus

8.100MPa

Strength

130MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

177787980

AKROMID®

C28 GF 25 FRT grey (8133)PA-Blend

AKROMID® C28 GF 25 FRT grey (8133) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend, colored in grey similar to RAL 7011. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications and certified to EN 45545-2 R6 and EN 45545-2 R1. To achieve an excellent surface quality a mould temperature of at least 120°C is necessary.

Features

flame retardant
surface modified
easy flow
public transportation

Regulatory

en45545-2

Properties

Modulus

11.000MPa

Strength

150MPa

Impact

Na

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,1 %

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 °C
800 °C
800 °C
850 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Protection Train

EN 45545-2

R1/6/7 HL2

General properties

Density

ISO 1183

23°C
1,44 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,9 - 1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
< 0,2 %
0,1 - 0,3 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more