Description

AKROTEKĀ®

Preliminary

PK-VM GF 10 FR orange (8745)

PK GF10 FR(40)

AKROTEKĀ® PK-VM GF 10 FR orange (8745) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.

Modulus

4.000MPa

Strength

70MPa

Impact

48kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 FR orange (8745) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.

AKROMIDĀ®

NEXT B3 GF 30 1 black (2485BMBCI)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 black (2485BMBCI) - PA 6, 30 % glass fiber, heat stabilised, high stiffness and strength, sustainable, biomass-balanced, technical parts in industrial engineering and automotive industry.

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 black (2485BMBCI) - PA 6, 30 % glass fiber, heat stabilised, high stiffness and strength, sustainable, biomass-balanced, technical parts in industrial engineering and automotive industry.

AKROMIDĀ®

UL

C3 GF 25 1 FR grey (8605)

PA66+PA6 GF25 FR(40)

AKROMIDĀ® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

Modulus

9.100MPa

Strength

125MPa

Impact

50kJ/mĀ²

AKROMIDĀ® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

AKROTEKĀ®

Preliminary

PK-VM GF 30 8 black (8783)

PK GF30

AKROTEKĀ® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

Modulus

8.100MPa

Strength

130MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

AKROMIDĀ®

UL

NEXT S3 GF 30 1 HU black (8825)

PA6.10 GF30

AKROMIDĀ® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/mĀ²

AKROMIDĀ® NEXT S3 GF 30 1 black (8825) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMIDĀ®

Preliminary

B28 GF 15 1 grey (8857)

PA6 GF15

AKROMIDĀ® B28 GF 15 1 grey (8857) - PA6, 15% glass fiber, heat stabilised, easy flowing, grey, industrial engineering, automotive.

Modulus

6.200MPa

Strength

110MPa

Impact

30kJ/mĀ²

AKROMIDĀ® B28 GF 15 1 grey (8857) - PA6, 15% glass fiber, heat stabilised, easy flowing, grey, industrial engineering, automotive.

AKROMIDĀ®

A3 GF 25 9 FR black (7957)

PA66 GF25 FR(40)

AKROMIDĀ® A3 GF 25 9 FR black (7957) is a 25% glass fibre reinforced, halogen free flame retardant polyamide 6.6.

Modulus

9.000MPa

Strength

140MPa

Impact

65kJ/mĀ²

AKROMIDĀ® A3 GF 25 9 FR black (7957) is a 25% glass fibre reinforced, halogen free flame retardant polyamide 6.6.

177787980

AKROMIDĀ®

A3 ICF 30 black (5021)PA66 CF30

AKROMIDĀ® A3 ICF 30 black (5021) is a 30% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Properties

Modulus

24.000MPa

Strength

240MPa

Impact

55kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
24000 MPa
15000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
240 MPa
170 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,8 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
22000 MPa
14000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
370 MPa
265 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,5 %
3,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
55 kJ/mĀ²
70 kJ/mĀ²
55 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
8 kJ/mĀ²
11 kJ/mĀ²
6 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
254 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,06 10ā»ā“/K
0,72 10ā»ā“/K

Thermal conductivity

DIN 52612

0,42 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
> 650 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,28 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
104 ā„¦
104 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more