AKROMID®
B3 GF 50 2 S1 black (3050)
PA6-I GF50
AKROMID® B3 GF 50 2 S1 black (3050) - PA 6, 50% glass fiber reinforced, impact modified, UV stabilised, housings and covers, automotive
15.000MPa
195MPa
110kJ/m²
AKROMID® B3 GF 50 2 S1 black (3050) - PA 6, 50% glass fiber reinforced, impact modified, UV stabilised, housings and covers, automotive
AKROMID®
T5 GF 20 8 black (6456)
PPA GF20
AKROMID® T5 GF 20 8 black (6456) - PPA, 20% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA
8.500MPa
160MPa
40kJ/m²
AKROMID® T5 GF 20 8 black (6456) - PPA, 20% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA
AKROMID®
T5 ICF 10 black (6772)
PPA CF10
AKROMID® T5 ICF 10 black (6772) is a 10% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties
12.000MPa
150MPa
25kJ/m²
AKROMID® T5 ICF 10 black (6772) is a 10% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties
AKROMID®
B3 ICF 20 1 L black (5296)
PA6 + PP CF20
AKROMID® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20
14.200MPa
140MPa
50kJ/m²
AKROMID® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20
AKROMID®
B25 GF 60 natural (8326)
PA6 GF60
AKROMID® B25 GF 60 natural (8326) - PA 6, easy flow, very high stiffness and strength, mechanical engineering, automotive.
22.000MPa
255MPa
100kJ/m²
AKROMID® B25 GF 60 natural (8326) - PA 6, easy flow, very high stiffness and strength, mechanical engineering, automotive.
AKROMID®
C3 GF 25 1 FR grey (8605)
PA66+PA6 GF25 FR(40)
AKROMID® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.
9.100MPa
125MPa
50kJ/m²
AKROMID® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.
AKROMID®
NEXT S3 GF 15 1 HU natural (8822)
PA6.10 GF15
AKROMID® NEXT S3 GF 15 1 HU natural (8822) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.
5.000MPa
110MPa
75kJ/m²
AKROMID® NEXT S3 GF 15 1 HU natural (8822) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.
AKROMID®
NEXT G3 GF 30 1 L CI natural (8377)PA6.9 + PP GF30
AKROMID® NEXT G3 GF 30 1 L CI natural (8377) is a 30% glass fiber reinforced PA 6.9/PP blend with high strength and stiffness. The partially bio-based grade is characterised by particularly low moisture absorption and high chemical resistance compared to classic PA 6 and PA 6.6. It is suitable for applications where weight reduction and sustainability are required. The material is certified according to ISCC PLUS. 34% of the fossil raw materials required for manufacturing this product were replaced by sustainable biomass-balanced PP (≙ allocation factor).
Features
Regulatory
Properties
8.000MPa
125MPa
65kJ/m²
Sustainability
Biobased carbon content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Melting temperature
ISO 11357-3
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.